We report on the fabrication of a boron-doped nanocrystalline diamond (NCD) 3 × 3 high-density microelectrode array (MEA) for amperometric measurements, with a single electrode area of 3 × 5 μm 2 and a separation in the μm scale. The NCD microelectrodes were grown by hot filament chemical vapor deposition (HFCVD) on a double-side polished sapphire wafer in order to preserve the diamond transparency. Bias enhanced nucleation (BEN) was performed to ensure a covalent adhesion of the films to the substrate. A current background noise of less than 5 pA peak to peak over a 1 kHz bandwidth resulted from an electrochemical investigation of the new device, using 100 mM KCl solutions and ferrocyanide red-ox couples. Cyclic voltammetry measurements in physiological buffer solution and in the presence of oxidizable biomolecules strengthened its suitability for bio-sensing. When compared to a 2 × 2 NCD microelectrode array prototype, already used for in vitro cell measurements, the signal to noise ratio of the amperometric response of the new 3 × 3 device proved twice as good. In addition, the optical transmittance of the boron-doped thin layers exceeded 40% in the visible wavelength range. The excellent electrochemical properties of NCD electrodes and the transparency in combination with the high spatial resolution make the new 3 × 3 NCD MEA a promising tool for electrochemical sensing in a variety of applications, ranging from medical to industrial, in neutral or harsh environments.
Lattice-matched InAlN/GaN high electron mobility transistors (HEMTs) have been prepared in a silicon-on-insulator (SOI)-like configuration. Here, this implies an ultrathin body 50 nm GaN channel/50 nm AlN nucleation layer material structure on sapphire with the active areas confined by mesa etching, resulting in semi-enhancement mode device characteristics. In contrast to conventional technologies, the device characteristics (maximum drain current, threshold voltage and 1 MHz large signal operation) change only within less than approx. 10% up to 600 • C compared to room temperature (RT). The current on/off ratio decreases from 10 10 at RT to 10 6 at 600 • C, due to residual defect activation. These first results of ultrathin body GaN-on-sapphire-based materials and device technology may indicate that essential improvements in the temperature-handling capability of electronic device structures beyond what is common at present may be possible with only limited sacrifice of device performance.
Here we report the first (as far as we know) experimental observation of extremely high enhancement factor due to elastic surface plasmon-polariton scattering by surface singularities.We have observed strong diffraction of surface plasmon-polaritons by shallow diffraction grating while its illumination by evanescent or volume waves do not shows any traces of diffraction structure in space distribution of scattered light.
A discrepancy between the theories of volume and surface plasmon-polaritons (SPPs) wave scattering was found. Its tentative explanation is related to the resonance-like emission of SPPs energy due to SPPs diffraction by a surface relief Fourier decomposition component. It was also shown that the sum of surface wave scattered intensity along a plane of incidence is proportional to surface roughness value.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.