In this work, a wet chemical etching technique has been used to estimate the depth of a p-n junction. The wet chemical etchant used is HF/HNO 3 /H 2 O solution. Subsequent to this process, optical and electron microscope imaging of crosssection was done to estimate the junction depth. This technique has been used for characterizing deep junction (up to 10 µm) formed by laser doping. Sheet resistances were measured after laser doping on 10 mm × 10 mm area with different scan speed from a heavily doped emitter. Sheet resistance reduces as scan speed is reduced. This indicates formation of deeper junction with lower scan speed. Selective emitter was prepared for chemical etching. Chemical etching leads to staining of n-type surface. An etching of 5 min reveals junction depths of different values from 1.8 -8.1 µm. The emitter fabricated by thermal diffusion as source for laser doping was measured to be 419 nm thick. SEM study shows clear difference between n and p-type region. Hence, this technique may be very useful when formation of a deep junction is expected or when SIMS study is very difficult.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.