Brittle intermetallics such as Cu6 Sn5 can be transformed into low cost, nonbrittle, superplastic and high temperature-resistant interconnection materials by sintering at temperatures more than 200 °C lower than its bulk melting point. Confirmed via in situ TEM heating, the sintered structure is pore-free with nanograins, and the interface is super-uniform.

No abstract

No abstract

No abstract

No abstract

Recently, nanosilver pastes have emerged as one of the most promising high temperature bonding materials for high frequency and high power applications, which provide an effective lead-free electronic packaging solution instead of high-lead and gold-based solders. Although nanosilver pastes can be sintered at lower temperature compared to bulk silver, applications of nanosilver pastes are limited by long-term sintering time (20–30 min), relative high sintering temperature (>250 °C), and applied external pressure, which may damage chips and electronic components. Therefore, low temperature rapid sintering processes that can obtain excellent nanosilver joints are anticipated. In this regard, we present a review of recent progress in the rapid sintering of nanosilver pastes. Preparation of nanosilver particles and pastes, mechanisms of nanopastes sintering, and different rapid sintering processes are discussed. Emphasis is placed on the properties of sintered joints obtained by different sintering processes such as electric current assisted sintering, spark plasma sintering, and laser sintering, etc. Although the research on rapid sintering processes for nanosilver pastes has made a great breakthrough over the past few decades, investigations on mechanisms of rapid sintering, and the performance of joints fabricated by pastes with different compositions and morphologies are still far from enough.

No abstract