This study aimed to evaluate the morphology and chemistry of an apatite layer induced by fast-set versus regular-set EndoSequence root repair materials using spectroscopic analysis. Holes of a 4 mm diameter were created in the root canal dentin, which were filled with the test material. Fetal calf serum was used as the incubation medium, and the samples incubated in deionized water were used as controls. The material-surface and material-dentin interfaces were analyzed after 28 days using Raman and infrared spectroscopy, scanning electron microscopy/energy dispersive X-ray, and X-ray diffraction. After incubation in fetal calf serum, both materials formed a uniform layer of calcium phosphate precipitate on their surfaces, with the dentinal interface. This precipitated layer was a combination of hydroxyapatite and calcite or aragonite, and had a high mineral maturity with the regular-set paste. However, its crystallinity index was high with the fast-set putty. Typically, both consistencies (putty and paste) of root repair material have an apatite formation ability when they are incubated in fetal calf serum. This property could be beneficial in improving their sealing ability for root canal dentin.
Aimed to evaluate the effect of water solubility on chemical properties and surface structure of bioceramic-based (BC-HiFlow and BC-EndoSeqence) compared with resin-based (Adseal) root canal sealers. Fresh mix was inserted into polyethylene mold (n = 10) and subjected to Vicat needle to evaluate the setting time. The set discs were analyzed by Fourier transform infrared (FTIR) spectroscopy then immersed in deionized water for 1, 7, 14 and 28 days. The solubility%, pH changes, released calcium (Ca2+), phosphate (PO43−) and silicon (Si4+) ions were evaluated after each immersion period. The discs were analyzed by scanning electron microscopy/Energy dispersed X-ray (SEM/EDX) before and after solubility test. Although FTIR detected similar composition of both bioceramic-sealers, BC-EndoSequence determined the prolonged setting times. At the end of solubility test, both bioceramic-sealers exhibited significant greater solubility (>3%), alkaline pH (>11) at p < 0.001. Adseal displayed the significant greatest Ca2+ and PO43− released, while BC-HiFlow displayed the significant greatest Si4+ release (p < 0.001). SEM revealed voids and pores on the surface of all tested sealers with the greatest value on Adseal surface. In conclusion, although both bioceramic-sealers had high solubility, BC-Hiflow complied the ISO standard regarding setting time and least surface micropores better than that of BC-EndoSequence.
For the management of necrotic immature teeth, regenerative endodontics offers the advantage of further root lengthening, thickening of dentin wall, and apical closure. This prospective study aimed to evaluate the long-term outcome of regenerative endodontics in immature necrotic permanent teeth. A total of 23 immature roots were medicated by triple antibiotic paste. After 21 days, bleeding was induced by over-instrumentation, and then mineral trioxide aggregate and coronal restoration were applied. Patients were scheduled for clinical and radiographic follow-up for 8 years. The radiographic changes of root dimensions were assessed using the ImageJ Plugin and statistically analyzed by Kruskal–Wallis test at a 95% confidence level. For qualitative evaluation, images were overlapped and analyzed using Photoshop software. All teeth were asymptomatic one month after the treatment. All teeth (n = 18) with preoperative periapical radiolucency showed complete resolution within 6–9 months. Recall rate at two, three, and eight years was 69.6%, 56.5%, and 34.8%, respectively. Continuous root development with a significant increase in root length and thickening of dentin wall accompanied by a significant decrease in apical canal diameter was seen at the end of the observation period (p < 0.001). In conclusion, the long-term outcome of regenerative endodontics revealed successful clinical and radiographic results with appropriate case selection.
This study evaluated the physicochemical properties and the effect of solubility on the surface morphology and composition of the root canal sealers MTA-Bioseal, MTA-Fillapex, and Adseal. Discs (n = 10) of freshly mixed sealer were prepared and then analyzed by Fourier transform infrared (FTIR) spectroscopy and scanning electron microscopy/energy-dispersive X-ray spectroscopy (SEM/EDX). The discs were immersed for 1, 7, 14, and 28 days in deionized water. The solubility %; pH change of the solution; and released calcium, phosphate, and silicon were measured for each period. The flowability and film thickness were also evaluated. Changes in the surface morphology and composition after 28 days of immersion were evaluated by SEM/EDX. The data were statistically analyzed by one-way ANOVA at p < 0.05. The FTIR and EDX results revealed similar compositions of MTA-Bioseal and MTA-Fillapex, but with different concentrations. The two MTA-based sealers had higher solution alkalinity (pH > 10) than Adseal (pH ≈ 8.5). MTA-Fillapex exhibited the highest solubility % and the largest calcium and silicon ion release. MTA-Bioseal had the highest phosphate ion release. After 28 days, the sealer surfaces showed large micropores, with larger pores in MTA-Fillapex. Adseal had an intermediate flowability but exhibited the greatest film thickness. Finally, the highest solubility and largest amount of silicon release was exhibited by MTA-Fillapex, which might predispose it to the development of large micropores, compromising the apical seal of obturation.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.