This study aimed to evaluate the morphology and chemistry of an apatite layer induced by fast-set versus regular-set EndoSequence root repair materials using spectroscopic analysis. Holes of a 4 mm diameter were created in the root canal dentin, which were filled with the test material. Fetal calf serum was used as the incubation medium, and the samples incubated in deionized water were used as controls. The material-surface and material-dentin interfaces were analyzed after 28 days using Raman and infrared spectroscopy, scanning electron microscopy/energy dispersive X-ray, and X-ray diffraction. After incubation in fetal calf serum, both materials formed a uniform layer of calcium phosphate precipitate on their surfaces, with the dentinal interface. This precipitated layer was a combination of hydroxyapatite and calcite or aragonite, and had a high mineral maturity with the regular-set paste. However, its crystallinity index was high with the fast-set putty. Typically, both consistencies (putty and paste) of root repair material have an apatite formation ability when they are incubated in fetal calf serum. This property could be beneficial in improving their sealing ability for root canal dentin.
Objectives. To analyse the chemistry and bioactivity of NeoMTA Plus in comparison with the conventional root repair materials. Method and Materials. Unhydrated and hydrated (initial and final sets) materials were analysed by Fourier transform infrared (FTIR) spectroscopy and X-ray diffraction (XRD). For bioactivity study, small holes of dentin discs were filled with either materials, immersed in PBS for 15 days, and analysed with FTIR and scanning electron microscope with energy dispersive X-ray (SEM/EDX). The calculation of crystallinity and carbonate/phosphate (CO 3 /PO 4 ) ratio of surface precipitates (from FTIR) and calcium/phosphate (Ca/P) ratio (from EDX) was statistically analysed using t-test or ANOVA, respectively, at 0.05 significance. Results. Both materials are tricalcium silicate-based that finally react to be calcium silicate hydrate. NeoMTA Plus has relatively high aluminium and sulfur content, with tantalum oxide as an opacifier instead of zirconium oxide in MTA Angelus. NeoMTA Plus showed better apatite formation, higher crystallinity and Ca/P but lower CO 3 /PO 4 ratio than MTA Angelus. SEM showed globular structure with a small particle size in NeoMTA Plus while spherical structure with large particle size in MTA Angelus. Conclusion. Due to fast setting, higher crystallinity, and better bioactivity of NeoMTA Plus, it can be used as a pulp and root repair material.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.