͑NH 4 ͒ 2 S x treatment was employed to enhance the efficiency of AlGaN metal-insulator-semiconductor ͑MIS͒ photodetectors ͑PDs͒ with a liquid phase deposited ͑LPD͒ SiO 2 layer. With ͑NH 4 ͒ 2 S x treatment, one can reduce the reverse leakage current of the PD by 2 orders of magnitude and enhance the effective Schottky barrier height from 0.77 to 0.86 eV. Also, the ͑NH 4 ͒ 2 S x treatment can also significantly reduce the interface state density, D it , at the AlGaN/LPD oxide interface. Photo-to-dark current ratio observed from the PDs with ͑NH 4 ͒ 2 S x treatment was also significantly larger.GaN-based semiconductor materials have been successfully used in high power, high frequency electronic devices and UV photodetectors ͑PDs͒ due to their excellent properties such as a high electron saturation velocity and a wide direct bandgap. Among the various GaN-based PDs, metal-semiconductor-metal ͑MSM͒ PD has attracted much attention due to its fabrication simplicity, low intrinsic capacitance, high operation speed, and low noise. 1-3 However, leakage current in GaN-based MSM-PDs is large because high dislocation density exists in GaN-based epitaxial layers prepared on sapphire substrate in general. 4 To solve this problem, one can insert an insulating layer between a metal and the underneath semiconductor. 5 For such metal-insulator-semiconductor ͑MIS͒ PDs, quality of the inserted insulator plays a very important role. GaN-based MIS PDs with various insulator materials, such as Al 2 O 3 , Ga 2 O 3 , SiO 2 , and insulator multilayer stacks, have all been reported. 6-13 Liquid phase deposition ͑LPD͒ is a reliable method to grow SiO 2 film on various semiconductor materials. Compared with other deposition methods, LPD SiO 2 film can be grown at a low temperature at an atmospheric pressure with low cost. The selective growth of the LPD SiO 2 film with a good step coverage is also possible.To further reduce leakage current in MIS PDs, we need to achieve a clean insulator/semiconductor interface. However, it is difficult to completely remove the native oxide on the surface of III-V compound semiconductors by standard cleaning methods. As a result, the high density of interface states is often observed in III-V compound semiconductor-based MIS devices. These interfacial states could cause the pinning of the surface Fermi level near the middle of the energy gap for the III-V MIS field effect transistors. These interfacial states could also result in a large leakage current in the III-V MIS PDs. It has been shown previously that ͑NH 4 ͒ 2 S x ͑S͒-treatment can prevent InP from oxidizing after cleaning. 14 Also, chemically bonded In-S species can be formed on the InP surface to assist the top InP layer in reconstructing its crystalline structure. Also, S-treatment can effectively passivate the surface of the AlInP window layer and thus enhance the conversion efficiency of III-V multijunction solar cells. 15 S-treatment also has a significant effect on GaN. Using X-ray photoelectron spectroscopy ͑XPS͒, Lin et al. found that nati...
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.