The present work investigated the use of biodegradable hydrogel composite scaffolds, based on the macromer oligo(poly(ethylene glycol) fumarate) (OPF), to deliver growth factors for the repair of osteochondral tissue in a rabbit model. In particular, bilayered OPF composites were used to mimic the structural layers of the osteochondral unit, and insulin-like growth factor-1 (IGF-1) and bone morphogenetic protein-2 (BMP-2) were loaded into gelatin microparticles and embedded within the OPF hydrogel matrix in a spatially controlled manner. Three different scaffold formations were implanted in a medial femoral condyle osteochondral defect: 1) IGF-1 in the chondral layer, 2) BMP-2 in the subchondral layer, and 3) IGF-1 and BMP-2 in their respective separate layers. The quantity and quality of osteochondral repair was evaluated at 6 and 12 weeks with histological scoring and micro-computed tomography (micro-CT). While histological scoring results at 6 weeks showed no differences between experimental groups, micro-CT analysis revealed that the delivery of BMP-2 alone increased the number of bony trabecular islets formed, an indication of early bone formation, over that of IGF-1 delivery alone. At 12 weeks post-implantation, minimal differences were detected between the three groups for cartilage repair. However, the dual delivery of IGF-1 and BMP-2 had a higher proportion of subchondral bone repair, greater bone growth at the defect margins, and lower bone specific surface than the single delivery of IGF-1. These results suggest that the delivery of BMP-2 enhances subchondral bone formation and that, while the dual delivery of IGF-1 and BMP-2 in separate layers does not improve cartilage repair under the conditions studied, they may synergistically enhance the degree of subchondral bone formation. Overall, bilayered OPF hydrogel composites demonstrate potential as spatially-guided, multiple growth factor release vehicles for osteochondral tissue repair.
In the last decade, the biomedical applications of nanoparticles (NPs) (e.g. cell tracking, biosensing, magnetic resonance imaging (MRI), targeted drug delivery, and tissue engineering) have been increasingly developed. Among the various NP types, superparamagnetic iron oxide NPs (SPIONs) have attracted considerable attention for early detection of diseases due to their specific physicochemical properties and their molecular imaging capabilities. A comprehensive review is presented on the recent advances in the development of in vitro and in vivo SPION applications for molecular imaging, along with opportunities and challenges.
The aim of this study was to develop new hydrophilic polyesters for tissue engineering applications. In our approach, poly(benzyloxymethyl glycolide-co-epsilon-caprolactone)s (pBHMG-CLs) were synthesized through melt copolymerization of epsilon-caprolactone (CL) and benzyl-protected hydroxymethyl glycolide (BHMG). Deprotection of the polymers yielded copolymers with pendant hydroxyl groups, poly(hydroxymethylglycolide-co-epsilon-caprolactone) (pHMG-CL). The synthesized polymers were characterized by GPC, NMR, and DSC techniques. The resulting copolymers consisting of up to 10% of HMG monomer were semicrystalline with a melting temperature above body temperature. Water contact angle measurements of polymeric films showed that increasing HMG content resulted in higher surface hydrophilicity, as evidenced from a decrease in receding contact angle from 68 degrees for PCL to 40 degrees for 10% HMG-CL. Human mesenchymal stem cells showed good adherence onto pHMG-CL films as compared to the more hydrophobic PCL surfaces. The cells survived and were able to differentiate toward osteogenic lineage on pHMG-CL surfaces. This study shows that the aforementioned hydrophilic polymers are attractive candidates for the design of scaffolds for tissue engineering applications.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.