To date, organic solar cells (OSCs) with the development of photovoltaic materials have realized high power conversion efficiencies (PCEs) through the solution processing strategy with bulk heterojunction (BHJ) structure, but the BHJ morphology is difficult to control in large-scale fabrication of OSCs. Herein, we report an alternative film-forming technology known as layer-bylayer (LbL). As compared to its BHJ counterpart, LbL presents many unique advantages including controllable ''p-i-n'' morphology, good charge transport and extraction properties, and great universality. By using the LbL-bladed coating strategy, a high PCE of 16.35% was achieved in the PM6:Y6 OSCs. Notably, a large-area solar module of 11.52 cm 2 with a geometrical fill factor of over 90% exhibited an outstanding PCE of 11.86%, which represents the highest efficiency of large-area solar modules. The results may pave the way for the fabrication of the photoactive layer in the future industrial production of OSCs.
A synergic interface design is demonstrated for photostable inorganic mixed‐halide perovskite solar cells (PVSCs) by applying an amino‐functionalized polymer (PN4N) as cathode interlayer and a dopant‐free hole‐transporting polymer poly[5,5′‐bis(2‐butyloctyl)‐(2,2′‐bithiophene)‐4,4′‐dicarboxylate‐alt‐5,5′‐2,2′‐bithiophene] (PDCBT) as anode interlayer. First, the interfacial dipole formed at the cathode interface reduces the workfunction of SnO2, while PDCBT with deeper‐lying highest occupied molecular orbital (HOMO) level provides a better energy‐level matching at the anode, leading to a significant enhancement in open‐circuit voltage (Voc) of the PVSCs. Second, the PN4N layer can also tune the surface wetting property to promote the growth of high‐quality all‐inorganic perovskite films with larger grain size and higher crystallinity. Most importantly, both theoretical and experimental results reveal that PN4N and PDCBT can interact strongly with the perovskite crystal, which effectively passivates the electronic surface trap states and suppresses the photoinduced halide segregation of CsPbI2Br films. Therefore, the optimized CsPbI2Br PVSCs exhibit reduced interfacial recombination with efficiency over 16%, which is one of the highest efficiencies reported for all‐inorganic PVSCs. A high photostability with a less than 10% efficiency drop is demonstrated for the CsPbI2Br PVSCs with dual interfacial modifications under continuous 1 sun equivalent illumination for 400 h.
NiO is a promising hole transporting material for perovskite solar cells due to its high hole mobility, good stability, easy processibility, and suitable Fermi level for hole extraction. However, the efficiency of NiO‐based cells is still limited by the slow hole extraction due to the poor perovskite/NiO interface and the inadequate quality of the two solution‐processed material phases. Here, large influences of a monolayer surface modification of NiO nanocrystal layers with ethanolamine molecules are demonstrated on the enhancement of hole extraction/transport and thus the photovoltaic performance. The underlying causes have been revealed by a series of studies, pointing to a favorable dipole layer formed by the molecular adsorption along with the enhanced perovskite crystallization and the improved interface contact. Comparatively, the solar cells based on a diethanolamine‐modified NiO layer have achieved a rather high fill factor, indeed one of the highest among NiO‐based perovskite solar cells, and high short‐circuit photocurrent density (Jsc), resulting in a power conversion efficiency of ≈16%, most importantly, without hysteresis.
All-polymer solar cells (all-PSCs) composed of conjugated polymers as both donor and acceptor components in bulk heterojunction photoactive layers have attracted increasing attention. However, it is a big challenge to achieve optimal morphology in polymer:polymer blends. In response, we report herein a new strategy to adjust the nanoscale organization for all-PSCs. Specifically, side chain engineering of the well-known naphthalene diimide (NDI)-based polymer N2200 is modulated by introducing a fraction of linear oligoethylene oxide (OE) side chains to replace branched alkyl chains on the NDI units and by synthesizing a series of NDI-based polymer acceptors NOE x, where x is the percentage of OE chain substituted NDI units relative to total NDI units. Compared to the reference polymer NOE0, OE-chain-containing polymer NOE10 offers a much higher power conversion efficiency (PCE) of 8.1% with a record high fill factor (FF) of 0.75 in all-PSCs. Moreover, the NOE10-based all-PSC exhibits excellent long-term and thermal stabilities with >97% of the initial PCE being maintained after 300 h of aging at 65 °C. This work demonstrates an effective morphology optimization strategy to achieve highly efficient and stable all-PSCs and shows the excellent potential of NOE10 as an alternative to commercially available acceptor polymers N2200.
An amino‐functionalized copolymer with a conjugated backbone composed of fluorene, naphthalene diimide, and thiophene spacers (PFN‐2TNDI) is introduced as an alternative electron transport layer (ETL) to replace the commonly used [6,6]‐Phenyl‐C61‐butyric acid methyl ester (PCBM) in the p–i–n planar‐heterojunction organometal trihalide perovskite solar cells. A combination of characterizations including photoluminescence (PL), time‐resolved PL decay, Kelvin probe measurement, and impedance spectroscopy is used to study the interfacial effects induced by the new ETL. It is found that the amines on the polymer side chains not only can passivate the surface traps of perovskite to improve the electron extraction properties, they also can reduce the work function of the metal cathode by forming desired interfacial dipoles. With these dual functionalities, the resulted solar cells outperform those based on PCBM with power conversion efficiency (PCE) increased from 12.9% to 16.7% based on PFN‐2TNDI. In addition to the performance enhancement, it is also found that a wide range of thicknesses of the new ETL can be applied to produce high PCE devices owing to the good electron transport property of the polymer, which offers a better processing window for potential fabrication of perovskite solar cells using large‐area coating method.
The high binding energy and low diffusion length of photogenerated Frenkel excitons have long been viewed as major drawbacks of organic semiconductors. Therefore, bulk heterojunction structure has been widely adopted to assist exciton dissociation in organic photon-electron conversion devices. Here, we demonstrate that these intrinsically “poor” properties of Frenkel excitons, in fact, offer great opportunities to achieve self-filtering narrowband organic photodetectors with the help of a hierarchical device structure to intentionally manipulate the dissociation of Frenkel excitons. With this strategy, filter-free narrowband organic photodetector centered at 860 nm with full-width-at-half-maximum of around 50 nm, peak external quantum efficiency around 65% and peak specific detectivity over 1013 Jones are obtained, which is one the best performed no-gain type narrowband organic photodetectors ever reported and comparable to commercialized silicon photodetectors. This novel device structure along with its design concept may help create low cost and reliable narrowband organic photodetectors for practical applications.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.