In this study, graphene oxide (GO) nanoflakes (0.5 and 1 wt%) were incorporated into a gelatin-hydroxyapatite (GHA) matrix through a freeze drying technique and its effect to enhance mechanical strength and osteogenic differentiation was studied. The GHA matrix with GO demonstrated less brittleness in comparison to GHA scaffolds. There was no significant difference in mechanical strength between GOGHA0.5 and GOGHA1.0 scaffolds. When the scaffolds were immersed in phosphate buffered saline (to mimic physiologic condition) for 60 days, around 50-60% of GO was released in sustained and linear manner and the concentration was within the toxicity limit as reported earlier. Further, GOGHA0.5 scaffolds were continued for cell culture experiments, wherein the scaffold induced osteogenic differentiation of human adipose derived mesenchymal stem cells without providing supplements like dexamethasone, L-ascorbic acid and β glycerophosphate in the medium. The level of osteogenic differentiation of stem cells was comparable to those cultured on GHA scaffolds with osteogenic supplements. Thus biocompatible, biodegradable and porous GO reinforced gelatin-HA 3D scaffolds may serve as a suitable candidate in promoting bone regeneration in orthopaedics.
As tissue engineering becomes more of a clinical reality through the ongoing bench to bedside transition, research in this field must focus on addressing relevant clinical situations. While most in vivo work in the area of bone tissue engineering focuses on bone regeneration within sterile, surgically created defects, there is a growing need for investigation of bone tissue engineering approaches within contaminated or scarred wound beds, such as those that may be encountered following traumatic injury or during delayed reconstruction/regeneration. Significant work has been performed in the area of local drug delivery via biomaterial carriers, but there is little intersection in the available literature between antibiotic delivery and tissue regeneration. In this review, we examine recent advances in segmental bone defect animal models, bone tissue engineering, and drug delivery with the goal of identifying promising approaches and areas needing further investigation towards developing both a better understanding and new tissue engineering approaches for addressing infection control while simultaneously initiating bone regeneration.
The study shows the development of a biodegradable bi-functional composite scaffold that can reduce bacterial infection, while promotes bone regeneration in osteomyelitis, without the need for revision surgery.
In this study, a two part bone tissue engineering scaffold was investigated consisting of a solid poly(propylene fumarate) (PPF) intramedullary rod for mechanical support surrounded by a porous PPF sleeve for osseointegration and delivery of poly(DL-lactic-co-glycolic acid) (PLGA) microspheres with adsorbed recombinant human bone morphogenetic protein-2 (rhBMP-2). Scaffolds were implanted into critical size rat segmental femoral defects with internal fixation for 12 weeks. Bone formation was assessed throughout the study via radiography, and following euthanasia via micro-CT and histology. Mechanical stabilization was evaluated further via torsional testing. Experimental implant groups included the PPF rod alone and the rod with a porous PPF sleeve containing PLGA microspheres with 0, 2, or 8 μg of rhBMP-2 adsorbed onto their surface. Results showed that presence of the scaffold increased mechanical stabilization of the defect, as evidenced by the increased torsional stiffness of the femurs by the presence of a rod compared to the empty defect. Although the presence of a rod decreased bone formation, the presence of a sleeve combined with a low or high dose of rhBMP-2 increased the torsional stiffness to 2.06 ± 0.63 N·mm and 1.68 ± 0.56 N·mm, respectively, from 0.56 ± 0.24 N·mm for the rod alone. The results indicate that, while scaffolds may provide structural support to regenerating tissues and increase their mechanical properties, the presence of scaffolds within defects may hinder overall bone formation if they interfere with cellular processes.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.