PURPOSE: This study evaluated the degree of conversion (DC) of four indirect resin composites (IRCs) with various compositions processed in different polymerization units and investigated the effect of thermal aging on the flexural strength and Vicker's microhardness. MATERIALS AND METHODS: Specimens were prepared from four IRC materials, namely Gr 1: Resilab (Wilcos); Gr2: Sinfony (3M ESPE); Gr3: VITA VMLC (VITA Zahnfabrik); Gr4: VITA Zeta (VITA Zahnfabrik) using special molds for flexural strength test (N = 80, n = 10 per group) (25 x 2 x 2 mm(3), ISO 4049), for Vicker's microhardness test (N = 80, n = 10 per group) (5 x 4 mm(2)) and for DC (N = 10) using FT-Raman Spectroscopy. For both flexural strength and microhardness tests, half of the specimens were randomly stored in distilled water at 37 degrees C for 24 hours (Groups 1 to 4), and the other half (Groups 5 to 8) were subjected to thermocycling (5000 cycles, 5 to 55 +/-1 degree C, dwell time: 30 seconds). Flexural strength was measured in a universal testing machine (crosshead speed: 0.8 mm/min). Microhardness test was performed at 50 g. The data were analyzed using one-way and two-way ANOVA and Tukey's test (alpha= 0.05). The correlation between flexural strength and microhardness was evaluated with Pearson's correlation test (alpha= 0.05). RESULTS: A significant effect for the type of IRC and thermocycling was found (p= 0.001, p= 0.001) on the flexural strength results, but thermocycling did not significantly affect the microhardness results (p= 0.078). The interaction factors were significant for both flexural strength and microhardness parameters (p= 0.001 and 0.002, respectively). Thermocycling decreased the flexural strength of the three IRCs tested significantly (p < 0.05), except for VITA Zeta (106.3 +/-9.1 to 97.2 +/-14 MPa) (p > 0.05) when compared with nonthermocycled groups. Microhardness results of only Sinfony were significantly affected by thermocycling (25.1 +/-2.1 to 31 +/-3.3 Kg/mm(2)). DC values ranged between 63% and 81%, and were not significantly different between the IRCs (p > 0.05). While a positive correlation was found between flexural strength and microhardness without (r = 0.309) and with thermocycling (r = 0.100) for VITA VMLC, negative correlations were found for Resilab under the same conditions (r =-0.190 and -0.305
AbstractPurpose: This study evaluated the degree of conversion (DC) of four indirect resin composites (IRCs) with various compositions processed in different polymerization units and investigated the effect of thermal aging on the flexural strength and Vicker's microhardness. Materials and Methods: Specimens were prepared from four IRC materials, namely Gr 1: Resilab (Wilcos); Gr2: Sinfony (3M ESPE); Gr3: VITA VMLC (VITA Zahnfabrik); Gr4: VITA Zeta (VITA Zahnfabrik) using special molds for flexural strength test (N = 80, n = 10 per group) (25 × 2 × 2 mm 3 , ISO 4049), for Vicker's microhardness test (N = 80, n = 10 per group) (5 × 4 mm 2 ) and for DC (N = 10) using FT-Raman Spectroscopy. For both fle...
Studies have shown that enamel can be modified by pulsed CO 2 laser to form a more acid-resistant substrate. This study evaluated the effects of a 10.6-μm CO 2 laser on enamel surface morphology and chemical composition as well as monitored intrapulpal temperature changes during irradiation. Human teeth were irradiated with fluences of 1.5 -11.5 J/cm 2 , and pulpal thermal as well as chemical and morphological modifications on enamel were assessed. The teeth were submitted to a pHcycling model, and the mineral loss was determined by means of cross-sectional microhardness. For all irradiated groups, intrapulpal temperature changes were below 3℃. FT -Raman spectroscopy and scanning electron microscopy indicated that fluences as low as 6.0 J/cm 2 were sufficient to induce chemical and morphological changes in enamel. Then, for fluences reaching or exceeding 10.0 J/cm 2 , laser-induced inhibitory effects on demineralization were observed. It was thus concluded that laser energy density in the range of 10.0 and 11.5 J/cm 2 could be applied to dental enamel in order to produce chemical and morphological changes and reduce the acid reactivity of enamel without compromising the pulp vitality.
We examine the morphological and chemical changes in the pulp chamber dentin after using endodontic agents by scanning electron microscopy (SEM), Fourier transform Raman spectroscopy (FT-Raman), and micro energy-dispersive x-ray fluorescence spectrometry (μEDXRF). Thirty teeth were sectioned exposing the pulp chamber and divided by six groups (n=5): NT-no treatment; CHX-2% chlorhexidine; CHXE-2% chlorhexidine+17% EDTA; E-17% EDTA; SH5-5.25% NaOCl; SH5E-5.25% NaOCl+17% EDTA. The inorganic and organic content was analyzed by FT-Raman. μEDXRF examined calcium (Ca) and phosphorus (P) content as well as Ca/P ratio. Impressions of specimens were evaluated by SEM. Data were submitted to Kruskal-Wallis and Dunn tests (p<0.05). Differences were observed among groups for the 960 cm(-1) peak. Ca and P content differences were significant (SH5>NT=SH5E>CHX>E>CHXE). CHXE and E presented the highest Ca/P ratio values compared to the other groups (p<0.05). The SEM images in the EDTA-treated groups had the highest number of open tubules. Erosion in the tubules was observed in CHX and SH5E groups. Endodontic agents change the inorganic and organic content of pulp chamber dentin. NaOCl used alone, or in association with EDTA, was the most effective agent considering chemical and morphological approaches.
The protective effect of Duofluorid® was significantly lower than fluoride gel against orange juice. The fluoride varnishes can interfere positively with the dissolution of dental enamel in the presence of acidic beverages. Fluoride gel showed the best protection level to extrinsic erosion with low costs.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.