Polymerization shrinkage stress of resin-based materials have been related to several unwanted clinical consequences, such as enamel crack propagation, cusp deflection, marginal and internal gaps, and decreased bond strength. Despite the absence of strong evidence relating polymerization shrinkage to secondary caries or fracture of posterior teeth, shrinkage stress has been associated with postoperative sensitivity and marginal stain. The latter is often erroneously used as a criterion for replacement of composite restorations. Therefore, an indirect correlation can emerge between shrinkage stress and the longevity of composite restorations or resin-bonded ceramic restorations. The relationship between shrinkage and stress can be best studied in laboratory experiments and a combination of various methodologies. The objective of this review article is to discuss the concept and consequences of polymerization shrinkage and shrinkage stress of composite resins and resin cements. Literature relating to polymerization shrinkage and shrinkage stress generation, research methodologies, and contributing factors are selected and reviewed. Clinical techniques that could reduce shrinkage stress and new developments on low-shrink dental materials are also discussed.
One of the clinically relevant problems dentists face when restoring endodontically treated teeth is the mismatch between fiber post and post space diameters, which results in an excessively thick resin cement layer. Fiber post relining appears as a solution for this problem.Objectives:The aim of this study was to evaluate the effect of fiber post relining with composite resin on push-out bond strength.Material and Methods:Twenty bovine incisors were selected to assess post retention. The crowns were removed below the cementoenamel junction and the root canals were treated endodontically and flared with diamond burs. The roots were allocated into two groups (n=10): G1: fiber posts without relining and G2: fiber posts relined with composite resin. The posts were cemented with a dual-cured resin cement and the specimens were sectioned transversally. Three 1.5-mm thick slabs were obtained per root and identified as cervical, medium and apical thirds. The push-out test was performed at a crosshead speed of 0.5 mm/min until post dislodgement occurred. The failure mode of fractured specimens was analyzed under scanning electron microscopy. Data were analyzed by split-plot ANOVA and post-hoc Tukey's test at a pre-set alpha of 0.05.Results:Relined fiber posts presented higher retention values than non-relined post in all thirds. No statistically significant differences (p>0.05) were found among thirds for relined posts. All failures occurred at the interface between resin cement and root dentin.Conclusions:Relining with composite resin seems to be an effective method to improve the retention of fiber posts to flared root canals.
Objective:The aim of this study was to evaluate the fracture strength and failure mode of flared bovine roots restored with different intraradicular posts.Material and Methods:Fifty bovine incisors with similar dimensions were selected and their roots were flared until 1.0 mm of dentin wall remained. Next, the roots were allocated into five groups (n=10): GI-cast metal post-and-core; GII-fiber posts plus accessory fiber posts; GIII- direct anatomic post; GIV- indirect anatomic post and GV- control (specimens without intraradicular post). A polyether impression material was used to simulate the periodontal ligament. After periodontal ligament simulation, the specimens were subjected to a compressive load at a crosshead speed of 0.5 mm/min in a servo-hydraulic testing machine (MTS 810) applied at 135° to the long axis of the tooth until failure. The data (N) were subjected to ANOVA and Tukey's post-hoc test (α=0.05).Results:GI and GIV presented higher fracture strength (p<0.05) than GII. GIII presented intermediate values without statistically significant differences (p>0.05) from GI, GII and GIV. Control specimens (GV) produced the lowest fracture strength mean values (p<0.05). Despite obtaining the highest mean value, GI presented 100% of unfavorable failures. GII presented 20% of unfavorable failures. GIII, GIV and GV presented only favorable failures.Conclusions:Although further in vitro and in vivo studies are necessary, the results of this study showed that the use of direct and indirect anatomic posts in flared roots could be an alternative to cast metal post-and-core.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.