In this study, artificial ageing of beech wood coated with Zn/ZnO particles by means of a cold plasma spraying process as well as coating systems including a Zn/ZnO layer and additional conventional sealings were examined. As ascertained by colour measurements, the particle coatings significantly decreased UV light-induced discolouration. Even though no significant colour changes were observed for particle-coated and alkyd-sealed samples, ATR-FTIR measurements revealed photocatalytic degradation of the alkyd matrix. In contrast, the polyurethane sealing appeared to be stabilised by the Zn/ZnO coating. Furthermore, morphologic properties of the pure particle coatings were studied by SEM and roughness measurements. SEM measurements confirmed a melting and solidifying process during deposition
Several previous studies have investigated the effects of heat treatment on the chemical composition, along with the physical and mechanical properties, of wood from various species. However, the effects of these property changes upon the machining properties and surface quality of machined wood have been studied much less. The main goal of this work was to investigate the comparative cutting power consumption during milling and the resulting surface roughness of heat-treated and untreated beech wood (Fagus sylvatica L.). Several cutting regimes were tested by combining different values of rotation speed, feed speed, and cutting depth. The cutting power and the processing roughness were assessed and compared. The results clearly showed that the cutting power involved in the milling of heat-treated beech wood was up to 50% lower than that of untreated wood, but the processing roughness was slightly higher.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.