No abstract

The feasibility of using hydrogen silsesquioxane (HSQ) to directly pattern the relief layer of step and flash imprint lithography (SFIL) templates has been successfully demonstrated. HSQ is a spin-coatable oxide, which is capable of high resolution electron-beam lithography. Negative acting and nonchemically amplified, HSQ has moderate electron-beam sensitivity and excellent processing latitude. In this novel approach, 6 ×6 × 0.25 in.3 quartz photomask substrates are coated with a 60 nm indium tin oxide (ITO) charge dissipation layer and directly electron-beam written using a 100 nm film of HSQ. Direct patterning of an oxide relief layer eliminates the problems of critical dimension control associated with both chromium and oxide etches, both required processes of previous template fabrication schemes. Resolution of isolated and semidense lines of 30 nm has been demonstrated on imprinted wafers using this type of template. During this evaluation, a failure of the release layer to provide a durable nonstick surface on ITO was discovered and investigated. This problem was successfully remedied by depositing a 5 nm oxide layer over the patterned ITO/HSQ template.

Previous work with the mechanical properties of step and flash imprint lithography etch barrier materials has shown bulk volumetric shrinkage trends that could impact imprinted feature dimensions and profile. This article uses mesoscopic and finite element modeling techniques to model the behavior of the etch barrier during polymerization. Model results are then compared to cross section images of template and etch barrier. Volumetric shrinkage is seen to impact imprinted feature profiles largely as a change in feature height.

No abstract

No abstract

Step and Flash Imprint Lithography (SFIL) is an attractive method for printing sub-100 nm geometries. Relative to other imprinting processes SFIL has the advantage that the template is transparent, thereby facilitating conventional overlay techniques. In addition, the imprint process is performed at low pressures and room temperature, minimizing magnification and distortion errors. The purpose of this work was to investigate alternative methods for defining high resolution SFIL templates and study the limits of the SFIL process. Two methods for fabricating templates were considered. The first method used a very thin (< 20 nm) layer of Cr as a hard mask. The second fabrication scheme attempts to address some of the weaknesses associated with a solid glass substrate. Because there is no conductive layer on the final template, SEM and defect inspection are compromised. By incorporating a conductive and transparent layer of indium tin oxide (ITO) on the glass substrate, charging is suppressed during SEM inspection, and the transparent nature of the final template is not affected. Using ZEP-520 as the electron beam imaging resist, features as small as 20 nm were resolved on the templates. Features were also successfully imprinted using both types of templates.

No abstract

No abstract