n - Zn O ∕ p - Ga N : Mg heterojunction light emitting diode (LED) mesas were fabricated on c-Al2O3 substrates using pulsed laser deposition for the ZnO and metal organic chemical vapor deposition for the GaN:Mg. High crystal quality and good surface morphology were confirmed by x-ray diffraction and scanning electron microscopy. Room temperature (RT) photoluminescence (PL) showed an intense main peak at 375nm and a negligibly low green emission indicative of a near band edge excitonic emission from a ZnO layer with low dislocation/defect density. The LEDs showed I-V characteristics confirming a rectifying diode behavior and a RT electroluminescence (EL) peaked at about 375nm. A good correlation between the wavelength maxima for the EL and PL suggests that recombination occurs in the ZnO layer and that it may be excitonic in origin. This also indicates that there is significant hole injection from the GaN:Mg into the ZnO.
Continued development of GaN-based light emitting diodes is being hampered by constraints imposed by current non-native substrates. ZnO is a promising alternative substrate but it decomposes under the conditions used in conventional GaN metal organic vapor phase epitaxy ͑MOVPE͒. In this work, GaN was grown on ZnO / c-Al 2 O 3 using low temperature/pressure MOVPE with N 2 as a carrier and dimethylhydrazine as a N source. Characterization confirmed the epitaxial growth of GaN. The GaN was lifted-off the c-Al 2 O 3 by chemically etching away the ZnO underlayer. This approach opens up the way for bonding of the GaN onto a support of choice.
Hybrid green light-emitting diodes (LEDs) comprised of n-ZnO/(InGaN/GaN) multi-quantum-wells/p-GaN were grown on semi-insulating AlN/sapphire using pulsed laser deposition for the n-ZnO and metal organic chemical vapor deposition for the other layers. X-ray diffraction revealed that high crystallographic quality was preserved after the n-ZnO growth. LEDs showed a turn-on voltage of 2.5 V and a room temperature electroluminescence (EL) centered at 510 nm. A blueshift and narrowing of the EL peak with increasing current was attributed to bandgap renormalization. The results indicate that hybrid LED structures could hold the prospect for the development of green LEDs with superior performance.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.