n - Zn O ∕ p - Ga N : Mg heterojunction light emitting diode (LED) mesas were fabricated on c-Al2O3 substrates using pulsed laser deposition for the ZnO and metal organic chemical vapor deposition for the GaN:Mg. High crystal quality and good surface morphology were confirmed by x-ray diffraction and scanning electron microscopy. Room temperature (RT) photoluminescence (PL) showed an intense main peak at 375nm and a negligibly low green emission indicative of a near band edge excitonic emission from a ZnO layer with low dislocation/defect density. The LEDs showed I-V characteristics confirming a rectifying diode behavior and a RT electroluminescence (EL) peaked at about 375nm. A good correlation between the wavelength maxima for the EL and PL suggests that recombination occurs in the ZnO layer and that it may be excitonic in origin. This also indicates that there is significant hole injection from the GaN:Mg into the ZnO.
We demonstrate 4.5 mW output power from AlGaN-based single quantum well ultraviolet light-emitting diodes at a very short wavelength of 267 nm in pulsed operation mode. The output power in continuous-wave mode reaches a value of 165 μW at an injected current of 435 mA. The measurements were done on arrays of four devices flip chip bonded to AlN submounts for thermal management.
We report AlGaN-based back-illuminated solar-blind ultraviolet p-i-n photodetectors with a peak responsivity of 136 mA/W at 282 nm without bias. This corresponds to a high external quantum efficiency of 60%, which improves to a value as high as 72% under 5 V reverse bias. We attribute the high performance of these devices to the use of a very-high quality AlN and Al0.87Ga0.13N/AlN superlattice material and a highly conductive Si–In co-doped Al0.5Ga0.5N layer.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.