Phase equilibria in the In–Pd–Sn system were investigated by a combination of key experiments and thermodynamic modeling. Partial isothermal sections at 500 °C and 800 °C of the In–Pd–Sn system for Pd contents above 66 at.% have been plotted experimentally using scanning electron microscopy with energy-dispersive X-ray spectroscopy (SEM/EDX) and X-ray diffraction (XRD). The solubility of the third component in binary compounds InPd3 and Pd3Sn was determined. The new ternary compound τ1 was found in Pd contents ranging from 20 to 25 at.% and at Sn contents varying from 5 to approximately 17 at.% Sn. This compound crystallizes in an Al3Ti-type tetragonal structure. Isostructural InPd2 and Pd2Sn phases from the In–Pd and Pd–Sn binary compositions form a continuous phase field in the ternary system at both temperatures. The temperatures of the solidus, liquidus, and phase transitions of the alloys along the Pd–In50Sn50 line were measured using DTA/DSC. Thermodynamic calculation of the In–Pd–Sn ternary system is performed using the CALPHAD method using the Thermo-Calc® software. The thermodynamic properties of the disordered fcc and liquid phases were described by the Redlich–Kister–Muggianu model. To describe intermetallic phases, namely, InPd3, Pd3Sn, τ1 and Pd2(InxSn1−x), a two-sublattice models was used. Thermodynamic description of the In–Pd–Sn system obtained in this study is in good agreement both with our results and the published experimental data
A new CuAu-type ternary phase (τ phase) is found in the AuPd-rich part of the Au-In-Pd system. It has a broad homogeneity range based on extensive (Pd,Au) and (In,Au) replacement, with the composition varying between AuInPd and AuInPd. The occupancies of the crystallographic positions were studied by single-crystal X-ray diffraction for three samples of different composition. The sites with m-3m symmetry are occupied by atoms with a smaller scattering power than the atoms located on 4/mmm sites. Two extreme structure models were refined. Within the first, the occupation type changes from (Au,In,Pd)(Pd,In) to (Au,Pd)(In,Pd,Au) with an increase in the Au gross content. For the second model, the occupation type (Au,In,Pd)(Pd,Au) remains essentially unchanged for all Au concentrations. Although the diffraction data do not allow the choice of one of these models, the latter model, where Au substitutes In on 4/mmm sites, seems to be preferable, since it agrees with the fact that the homogeneity range of the τ phase is inclined to the Au corner and provides the same occupation type for all the studied samples of different compositions.
A combination of physicochemical analysis methods is used to study the phase equilibria in the Cu-In-Pd system. An isothermal section at 800°C has been constructed. The copper solubility in the binary phases of the In-Pd system is determined.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.