This study assesses in vivo the surface roughness necessary to reduce plaque colonization on titanium after 24 hours. Three groups of 16 titanium disks were assigned to 3 different polishing groups (A, B, and C). The roughness was evaluated with a laser profilometer and the morphology with a scanning electron microscope (SEM). Eight volunteers were enrolled and two Stents were applied in the mandibular posterior region of each. Each Stent supported 3 disks, one per group. The volunteers suspended oral hygiene for 24 hours, after which the Stents were removed; one was processed for evaluation of the adherent biomass and the other for SEM study. On each specimen a global area of 100 × 125 μm was examined with SEM. The area was composed of five 20 × 25 μm randomly selected fields. For each field the density of bacteria and the morphotypes were recorded. The data quoted for the global area are cumulative of those observed in the 20 × 25 μm fields. Group A had a significantly smoother surface than groups B and C. The adherent microbial biomass determination and SEM evaluation revealed that group A contained less bacteria than the roughest group. The bacterial population was composed of cocci in group A, and of cocci and short and long rods in groups B and C. We conclude that a titanium surface with Ra ≤ 0.088 μm and Rz < 1.027 μm strongly inhibits accumulation and maturation of plaque at the 24‐hour time period and that such smoothness can be achieved in transgingival and healing implant components. J Periodontol 1997;68:556–562.
Demineralization of dental hard tissue is a widespread problem and the main responsible for dental caries and dentin hypersensitivity. The most promising strategies to induce the precipitation of new mineral phase are the application of materials releasing gradually Ca2+ and PO43− ions or mimicking the mineral phase of the host tissue. However, the design of formulations covering both processes is so far a challenge in preventive dentistry. In this work, we have synthesized innovative biomimetic amorphous calcium phosphate (ACP), which has been, for the first time, doped with fluoride ions (FACP) to obtain materials with enhanced anti-caries and remineralizing properties. Significantly, the doping with fluoride (F) did not vary the physico-chemical features of ACP but resulted in a faster conversion to the crystalline apatite phase in water, as observed by in-situ time-dependent Raman experiments. The efficacy of the as synthesized ACP and FACP samples to occlude dentinal tubules and induce enamel remineralization has been tested in vitro in human molar teeth. The samples showed good ability to partially occlude the tubules of acid-etched dentin and to restore demineralized enamel into its native structure. Results demonstrate that ACP and FACP are promising biomimetic materials in preventive dentistry to hinder demineralization of dental hard tissues.
The aim of this in vitro study was to evaluate the influence of physicochemical surface properties of resin-based composites on Streptococcus mutans biofilm formation. Specimens were prepared from each of four resin-based composites by polymerization against Mylar strips. Half of the number of specimens received no further surface treatment, whereas the other half were subjected to a polishing treatment. Surface roughness (SR) and topography were assessed using profilometry and atomic force microscopy. Surface free-energy (SFE) was determined, and the chemical surface composition was analysed by X-ray photoelectron spectroscopy (XPS). S. mutans biofilms were formed on the surface of the resin-based composite specimens for either 48 or 96 h using an artificial mouth system (AMS). Polishing caused a significant decrease in SFE, and XPS analysis indicated an increase of surface silicon and a decrease of surface carbon. Only for Grandio was a significant increase in SR identified after polishing, which was probably related to the higher concentration of filler particles on its surface. Significantly less S. mutans biofilm formation was observed on polished resin-based composites than on unpolished resin-based composites. These results indicate that the proportions of resin matrix and filler particles on the surface of resin-based composites strongly influence S. mutans biofilm formation in vitro, suggesting that minimization of resin matrix exposure might be useful to reduce biofilm formation on the surface of resin-based composites.
Background. The use of dental handpieces produces aerosols containing microbial agents, bacteria, and viruses representing a high-risk situation for airborne cross infections. The aim of this study was to map and quantify the biological contamination of a dental operatory environment using a biological tracer.Methods. Streptococcus mutans suspension was infused into the mouth of a manikin, and an operator performed standardized dental procedures using an air turbine, a contra-angle handpiece, or an ultrasonic scaler. The presence of the tracer was measured at 90 sites on the dental unit and the surrounding surfaces of the operatory environment.Results. All tested instruments spread the tracer over the entire dental unit and the surrounding environment, including the walls and ceiling. The pattern and degree of contamination were related to the distance from the infection source. The maximum distance of tracer detection was 360 centimeters for air turbine, 300 cm for contra-angle handpiece, and 240 cm for ultrasonic scaler. No surface of the operative environment was free from the tracer after the use of the air turbine.Conclusions. Attention should be paid to minimize or avoid the use of rotary and ultrasonic instruments when concerns for the airborne spreading of pandemic disease agents are present.Practical Implications. This study supports the recommendations of dental associations to avoid treatments generating aerosols, especially during pandemic periods. Guidelines for the management of dental procedures involving aerosols, as well as methods for the modification of aerosols aimed to inactivate the infective agent, are urgently needed.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.