No abstract

No abstract

Background: Concrete is a common material used in the construction of marine structures, such as bridges, water treatment plants, jetties, etc. The use of concrete in these environment exposes it to attack from chemicals like sulphates, chlorides and alkaline, thereby causing it to deteriorate, and unable to perform satisfactorily within its service life. Hence, the need to investigate the durability properties of concrete has become necessary especially when admixtures are used to modify some of its properties. Objective: This research work investigates the effect of Cassava Starch (CS) on the durability characteristics of concrete. Methods: The durability properties investigated in this work are water absorption, sorptivity, resistance to sulphates, sodium hydroxides and chloride penetration. The specimens were prepared by adding CS by weight of cement at 0.4, 0.8, 1.2, 1.6 and 2.0% respectively. The concrete specimens were cured for 28 days, tested for compressive strength before ponding in ionic solutions of sodium hydroxide, sulphuric acid and sodium chloride. Six (6) concrete mixes were prepared, five of which were used to evaluate the effect of CS on the durability characteristics of concrete. Results: The slump values reduced with the increasing dosage of CS due to the viscous nature of the CS paste. Generally, the addition of CS in concrete tends to improve the resistance of concrete to sulphate and chloride attack due to the ability of the muddy-like starch gel to block the pore spaces of hardened concrete, hence, reduces the rate at which water and other aggressive chemicals penetrate the concrete. In addition, the retarding ability of CS impedes the formation of mono-sulphate aluminates during cement hydration, thereby making the concrete less susceptible to sulphate attack. Conclusion: The addition of CS to concrete by weight of cement generally improved the durability characteristics of concrete, while the relative performances of the concrete mixes showed that CS 2.0 gave a better resistance to chloride penetration and sulphate attack.

No abstract

Background: Concrete is a widely used material in construction, which has given rise to innovations in terms of modifying some of its properties to meet desired requirements. The use of chemical admixtures is important in this regard, which has necessitated the search for new materials which can serve as a substitute. Objective: This research work investigates the use of Cassava Starch (CS) as an admixture for improving the physical and mechanical properties of concrete. Methodology: The physical and mechanical properties of concrete were studied by adding CS by weight of cement at 0.4, 0.8, 1.2, 1.6 and 2.0%, respectively. Concrete cubes and cylinders were cast and cured for a test period of 7, 14, 28, 56 and 90 days, respectively. Unreinforced beams of size 150 x 150 x 530 were cast and cured for 28 days. A total of 6 mix proportion was used, five out of which were used to examine the effect of CS on the properties of concrete. Results: The workability of concrete reduced as the percentage of CS increased due to its viscosity modifying properties. CS increased the initial and final setting time of concrete for every increase in percentage addition. An improvement in the compressive strength, split tensile strength, flexural strength and elastic modulus of concrete were noticed for cassava starch-modified concrete over the control for some of the mixes at all days of curing. The density of concrete was found to decrease at 1.6 and 2.0% addition of CS in concrete. Conclusion: From the results of this investigation, CS improved the compressive, split tensile, flexural and elastic modulus of concrete at an optimum of 0.8 percentage addition of CS. The setting time of concrete was also increased, which makes CS suitable to be used as a retarding admixture in hot weather concreting. Based on the findings of the work, CS can be considered as an admixture to be used as a substitute for retarders and viscosity modifying admixtures for improved concrete properties.

This paper presents the properties of concrete made with cement partially replaced with rice straw ash and eggshell ash. The rice straws and eggshells were incinerated, sieved, and ground, and the physical and chemical properties of the resultant ash and the other materials incorporated in the concrete mixes were determined. A class 35 concrete mix with no partial replacement of cement with rice straw ash designed with the British Research Establishment method with a water/cement ratio of 0.5 was considered as the control mix. The cement in concrete was partially replaced with rice straw ash by 5% to 30% and its compressive and splitting tensile strength was determined after 7, 14, 28, 56, and 90 days of curing. Durability, resistance to acid attack, and other wet and hardened properties of concrete with cement partially replaced with rice straw ash were also determined. An increase in compressive strength above the control mix was observed for concrete with 5% and 10% partial replacement of cement with rice straw ash. When eggshell ash was added to concrete mixes made with cement partially replaced with rice straw ash at 15% and 20%, the 28, 56, and 90-day compressive strength was found to increase. It can be concluded that rice straw and eggshell ash can be used to partially replace cement in concrete and result in a concrete whose properties compare favorably with control

No abstract

Transverse openings are often provided to reinforced concrete beams to accommodate utility ducts and pipes. This technique is usually adopted to avoid the creation of dead space in structures caused by extended dropped ceilings and leads to significant cost saving. On the other hand, the provision of openings through a beam creates a reduction in its strength and affects serviceability. In this study, ten reinforced concrete beams were cast using C30 concrete. Material characterization and engineering properties tests were carried out to ensure compliance with the requirements provided by the codes of practice. The effect of vertical positioning and size of openings was investigated through subjecting the beams to a four-point bending test after 28 days of curing. Maximum load capacity, first cracking load, and deflections at mid-span were recorded and crack pattern and failure mode were evaluated. Test data showed that openings of depth greater than 0.4d significantly affect the beams’ strength and lead to earlier cracking, while the failure mode remains essentially the same, a diagonal tension crack through the opening except for opening of 0.5d size where the failure occurred by a sudden formation of two independent shear cracks above and below the opening. When holes were located above the centroid of the section, the beams exhibited a lesser deflection characterized by the absence of plastic deformation. Furthermore, a significant reduction in strength was recorded compared to cases where the positioning of openings was in tension chords. This was validated using equations from the ACI code of reinforced concrete design.