Background: Concrete is a common material used in the construction of marine structures, such as bridges, water treatment plants, jetties, etc. The use of concrete in these environment exposes it to attack from chemicals like sulphates, chlorides and alkaline, thereby causing it to deteriorate, and unable to perform satisfactorily within its service life. Hence, the need to investigate the durability properties of concrete has become necessary especially when admixtures are used to modify some of its properties. Objective: This research work investigates the effect of Cassava Starch (CS) on the durability characteristics of concrete. Methods: The durability properties investigated in this work are water absorption, sorptivity, resistance to sulphates, sodium hydroxides and chloride penetration. The specimens were prepared by adding CS by weight of cement at 0.4, 0.8, 1.2, 1.6 and 2.0% respectively. The concrete specimens were cured for 28 days, tested for compressive strength before ponding in ionic solutions of sodium hydroxide, sulphuric acid and sodium chloride. Six (6) concrete mixes were prepared, five of which were used to evaluate the effect of CS on the durability characteristics of concrete. Results: The slump values reduced with the increasing dosage of CS due to the viscous nature of the CS paste. Generally, the addition of CS in concrete tends to improve the resistance of concrete to sulphate and chloride attack due to the ability of the muddy-like starch gel to block the pore spaces of hardened concrete, hence, reduces the rate at which water and other aggressive chemicals penetrate the concrete. In addition, the retarding ability of CS impedes the formation of mono-sulphate aluminates during cement hydration, thereby making the concrete less susceptible to sulphate attack. Conclusion: The addition of CS to concrete by weight of cement generally improved the durability characteristics of concrete, while the relative performances of the concrete mixes showed that CS 2.0 gave a better resistance to chloride penetration and sulphate attack.

Background: Concrete is a widely used material in construction, which has given rise to innovations in terms of modifying some of its properties to meet desired requirements. The use of chemical admixtures is important in this regard, which has necessitated the search for new materials which can serve as a substitute. Objective: This research work investigates the use of Cassava Starch (CS) as an admixture for improving the physical and mechanical properties of concrete. Methodology: The physical and mechanical properties of concrete were studied by adding CS by weight of cement at 0.4, 0.8, 1.2, 1.6 and 2.0%, respectively. Concrete cubes and cylinders were cast and cured for a test period of 7, 14, 28, 56 and 90 days, respectively. Unreinforced beams of size 150 x 150 x 530 were cast and cured for 28 days. A total of 6 mix proportion was used, five out of which were used to examine the effect of CS on the properties of concrete. Results: The workability of concrete reduced as the percentage of CS increased due to its viscosity modifying properties. CS increased the initial and final setting time of concrete for every increase in percentage addition. An improvement in the compressive strength, split tensile strength, flexural strength and elastic modulus of concrete were noticed for cassava starch-modified concrete over the control for some of the mixes at all days of curing. The density of concrete was found to decrease at 1.6 and 2.0% addition of CS in concrete. Conclusion: From the results of this investigation, CS improved the compressive, split tensile, flexural and elastic modulus of concrete at an optimum of 0.8 percentage addition of CS. The setting time of concrete was also increased, which makes CS suitable to be used as a retarding admixture in hot weather concreting. Based on the findings of the work, CS can be considered as an admixture to be used as a substitute for retarders and viscosity modifying admixtures for improved concrete properties.