Chronic wounds are a global health problem, and their treatments are difficult and long lasting. The development of medical devices through tissue engineering has been conducted to heal this type of wound. In this study, it was demonstrated that the combination of natural and synthetic polymers, such as poly (D-L lactide-co-glycolide) (PLGA) and gelatin (Ge), were useful for constructing scaffolds for wound healing. The aim of this study was to evaluate the influence of different PLGA/gelatin ratios (9:1, 7:3 and 5:5 (v/v)) on the physical, chemical and biological properties of electrospun scaffolds for wound dressings. These PLGA/Ge scaffolds had randomly oriented fibers with smooth surfaces and exhibited distances between fibers of less than 10 μm. The 7:3 and 5:5 PLGA/Ge scaffolds showed higher swelling, hydrophilicity and degradation rates than pure PLGA and 9:1 (v/v) PLGA/Ge scaffolds. Young’s moduli of the scaffolds were 72 ± 10, 48 ± 6, 58 ± 6 and 6 ± 1 MPa for the pure PLGA scaffold and the 9:1, 7:3 and 5:5 (v/v) PLGA/Ge scaffolds, respectively. Mesenchymal stem cells (MSCs) seeded on all the PLGA/Ge scaffolds were viable, and the cells were attached to the fibers at the different analyzed timepoints. The most significant proliferation rate was observed for cells on the 7:3 PLGA/Ge scaffolds. Biocompatibility analysis showed that all the scaffolds produced inflammation at the first week postimplantation; however, the 7:3 and 5:5 (v/v) PLGA/Ge scaffolds were degraded completely, and there was no inflammatory reaction observed at the fourth week after implantation. In contrast, the 9:1 PLGA/Ge scaffolds persisted in the tissue for more than four weeks; however, at the eighth week, no traces of the scaffolds were found. In conclusion, the scaffolds with the 7:3 PLGA/Ge ratio showed suitable physical, chemical and biological properties for applications in chronic wound treatments.
Modelado de la biodegradación en biorreactores de lodos de hidrocarburos totales del petróleo intemperizados en suelos y sedimentos (Biodegradation modeling of sludge bioreactors of total petroleum hydrocarbons weathering in soil and sediments)
Most cells in the human body grow and live in a complex network of biomaterials usually known as the extracellular matrix, which is composed of various proteins and proteoglycans assembled into a highly ordered structure [1-3]. In regenerative medicine, when new tissue needs to be grown intra or extra corporally, there are fundamental aspects to be considered for the construction, development and functionality of living tissue: bioactive molecules together with a scaffold, used as a support for the cells, are needed to mimic the extracellular matrix and promote cell adhesion, proliferation, differentiation, and migration pathways [4,5]. Producing scaffolds for tissue engineering demands the development of new materials with bioactive molecules and an appropriated technique. Among the techniques to produce polymeric scaffolds, electrospinning is a simple and effective method to obtain nanofiber-based scaffolds resembling the functions of the extracellular matrix [6-10]. Regarding the materials, a number of natural and synthetic polymers have been used to produce electrospun scaffolds [11-15]. Poly (lactic acid) (PLA) is widely used for the generation of scaffolds for tissue engineering to allow precise control over their physicochemical and mechanical properties but exhibit limited cellular affinity. Natural biodegradable polymers, such as collagen, provide inherent binding sites for the promotion of cell adhesion and cellular growth. However, this natural material, obtained from animal or human tissues, is expensive and
In this work, chitosan (CS)/poly (vinyl alcohol) (PVA) nanofibers were prepared by using the electrospinning method. Different CS concentrations (0.5, 1, 2, and 3 wt %), maintaining the PVA concentration at 8 wt %, were tested. Likewise, the studied electrospinning experimental parameters were: syringe/collector distance, solution flow and voltage. Subsequently, the electrospun fibers were collected on a reticulated vitreous carbon (RVC) support for 0.25, 0.5, 1, 1.5, and 2 h. The morphology and diameter of the CS/PVA nanofibers were characterized by scanning electron microscopy (SEM), finding diameters in the order of 132 and 212 nm; the best results (uniform fibers) were obtained from the solution with 2 wt % of chitosan and a voltage, distance, and flow rate of 16 kV, 20 cm, and 0.13 mL/h, respectively. Afterwards, a treatment with an ethanolic NaOH solution was performed, observing a change in the fiber morphology and a diameter decrease (117 ± 9 nm).
Physical properties of porous membranes made of biocompatible and biodegradable polymers have been studied. The membranes are intended to be used as scaffolds for the regeneration of soft and hard tissues. Polylactides, polycaprolactone and some of their derivates are biocompatible as well as biodegradable materials, and are used for the preparation of nanofibers and nanoporous membranes. These membranes also have comparative advantages as cellular scaffolds for tissue engineering since they can be prepared to mimic the morphology of the extra cellular matrix.Chemical, physical, and biological properties of microfibers and scaffolds of polylactic acid (PLLA), as well as PLLA modified with hydroxyapatite nanoparticles and collagen (Col) are reported in this paper. The microfibers and the scaffolds were prepared by electrospinning. Morphology, diameter and porosity of the scaffold were determined by scanning electron microscopy and an image analyzer program. The microfibers are semicrystalline showing a shell of crystalline nanofibrils. The diameter of the fibers varied between 100 and 800 nm and the porous area of the membrane is between 60 and 80%. The mechanical properties of the microfibers and scaffolds were evaluated by microtensile tests and their behavior was simulated by using an original multiscale asymptotic homogenization model. Cultures of mesenchymal stem cells were used to evaluate their biological activity. Cell adhesion was observed in the modified PLLA scaffolds with grafted hydroxyapatite.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.