Pit nucleation on as-cast aluminiuim alloy AW-5083 in 0.01M NaCl

Abstract

The use of aluminium alloys in a wide range of technical applications is related mostly to the two facts: they facilitate weight saving of final products (if compared to the steel) and they are prone to spontaneous passivity due to the coherent surface oxide layer which impedes further reaction of aluminium with the environment. Among the commercial Al alloys, EN AW-5083 alloy is a representative non-heat treatable Al-Mg based alloy which possesses many interesting characteristics as a structural material, such as low price, moderately high strength, high formability in conjunction with superplasticity and good corrosion resistance in marine atmospheres. Aiming to enhance the knowledge of possible interactions of studied alloy EN AW-5083 in as-cast condition with chloride media, electrochemical measurements were used to follow the pitting behaviour in 0.01 M NaCl. The results of tests have shown that susceptibility of alloy to pitting corrosion is strongly influenced by the microstructural constituents of the alloy in as-cast condition

Influence of seawater composition on SCC behavior of anodized 1050 Al‐alloy

“…The aluminium alloys of the 1xxx series are widely used in many commercial applications and therefore studies of these alloys are important in clarifying the effects of the constituents of high strength alloys on SCC behaviour (Trueba and Trasatti, 2009;Braun, 1995;Zhu and Van Ooij, 2003;Dolic et al, 2011;Dollah and Robinson, 2011).…”

“…The stress corrosion cracking (SCC) behaviour of aluminium alloys in aqueous environments such marine waters is of great importance for industrial applications. The aluminium alloys of the 1xxx series are widely used in many commercial applications and therefore studies of these alloys are important in clarifying the effects of the constituents of high strength alloys on SCC behaviour (Trueba and Trasatti, 2009; Braun, 1995; Zhu and Van Ooij, 2003; Dolic et al , 2011; Dollah and Robinson, 2011).…”

Solidification characteristics of atomized AlCu4Mg1-SiC composite powders

“…Aluminum and its alloys are remarkable for structural applications due to the requirements of lighter and stronger materials [4][5]. Powder metallurgy and mechanical alloying are sophisticated technologies for structural hardening of Albased alloys.…”

Parâmetros térmicos e microestruturais na solidificação transitória de Ligas Al-Mg e Al-Mg-Si e correlação com resistências mecânicas e à corrosão

“…A morfologia, composição química e a distribuição das fases secundárias, formadas durante o processo de solidificação ou tratamentos termomecânicos, e dispostas na matriz de ligas de alumínio são conhecidas por induzir a corrosão localizada (Dorina et al, 2015;Birbilis et al, 2005;Proton et al, 2014;. Birbilis A presença de nanopartículas precipitadas e microimpurezas na superfície de ligas de alumínio tende a induzir a reação catódica, consequentemente, ocorre dissolução anódica de áreas adjacentes, pontos de nucleação de corrosão por pite (Dolić et al, 2011). Partículas intermetálicas, tais como Al 2 Cu Al 3 Fe favorecem a formação de células electroquímicas locais entre elas e a matriz rica em alumínio (Dolić et al, 2011).…”

“…Birbilis A presença de nanopartículas precipitadas e microimpurezas na superfície de ligas de alumínio tende a induzir a reação catódica, consequentemente, ocorre dissolução anódica de áreas adjacentes, pontos de nucleação de corrosão por pite (Dolić et al, 2011). Partículas intermetálicas, tais como Al 2 Cu Al 3 Fe favorecem a formação de células electroquímicas locais entre elas e a matriz rica em alumínio (Dolić et al, 2011). Certos fatores podem ser associados com corrosão por pites em ligas de Al, a exemplo, o tipo e concentração íon agressivo, o pH do meio, a temperatura, ou ainda as características estruturais do filme de óxido passivo.…”