The effect of stress due to the lattice misfit in the Cu/Au interface has been studied by carrying out molecular dynamics simulations. Results show that the stress can induce stacking faults to relieve the stress.
The microstructure and magnetic viscosity of bulk amorphous Nd60Fe20Al5Co10B5,prepared by suction casting the molten alloy into a copper mold under an argon atmosphere, have been investigated. The results show that clusters with size 3–5 nm are found to be embedded in the amorphous matrix of as-cast bulk amorphous Nd60Fe20Al5Co10B5 alloy. The Nd60Fe20Al5Co10B5 alloy shows hard magnetic behavior at room temperature, with an intrinsic coercivity of 360 kA/m and a remanence of 69.39 mT. The magnetic viscosity of bulk amorphous Nd60Fe20Al5Co10B5 has been investigated on the major hysteresis loop, and simple logarithmic time dependence is observed. A value for the fluctuation field of 8.24 kA/m is obtained. Analysis based on a Henkel plot is used to confirm the existence of magnetic interaction among clusters. The coercivity mechanism responsible for the hard magnetic behavior of bulk amorphous Nd60Fe20Al5Co10B5 alloy is also discussed.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.