We demonstrate the hybrid fabrication process of a graphene integrated highly transparent resistive random-access memory (TRRAM) device. The indium tin oxide (ITO)/Al2O3/graphene nonvolatile memory device possesses a high transmittance of >82% in the visible region (370-700 nm) and exhibits stable and non-symmetrical bipolar switching characteristics with considerably low set and reset voltages (<±1 V). The vertical two-terminal device shows an excellent resistive switching behavior with a high on-off ratio of ∼5 × 103. We also fabricated a ITO/Al2O3/Pt device and studied its switching characteristics for comparison and a better understanding of the ITO/Al2O3/graphene device characteristics. The conduction mechanisms in high and low resistance states were analyzed, and the observed polarity dependent resistive switching is explained based on electro-migration of oxygen ions.
Magnetoelectric (ME) composite thin films are promising candidates for novel applications in future nanoelectronics, spintronics, memory, and other multifunctional devices as they exhibit much higher ME coupling and transition temperatures (Tc) than well-known single phase multiferroics discovered to date. Among the three types of multiferroic composite nanostructures, (2–2) layered and (1–3) vertically aligned composite nanostructures exhibit comparatively smaller ME coupling due to different shortcomings that restrict their use in many applications. Here, we study the morphological, piezoresponse force microscopic (PFM), ferroelectric, magnetic, and magnetodielectric properties of 0–3 [magnetic nanoparticles (0) homogeneously distributed in ferroelectric matrices (3)] multiferroic composite thin films. The Pb(Fe0.5Nb0.5)O3 (PFN)–Ni0.65Zn0.35Fe2O4 (NZFO) particulate composite films were synthesized by pulsed laser deposition. These particulate composite thin films are completely c-axis oriented with very low surface roughness. We observed magnetic and ferroelectric Tc above room temperature (RT) for all composite thin films. The PFN–NZFO 0–3 composites exhibit large polarization, high saturated magnetization with low coercive field, and low dielectric loss along with magnetodielectric coupling at RT. These nanocomposites might be utilized in next generation nano/microelectronics and spintronic devices.
Magnetoelectric (ME) materials with ferroelectric and magnetic transition temperatures near room temperature are of current interest in research due to their technological importance and potential applications. Herein, we report the coupled magnetic ordering and phonons in gallium ferrite (GaFeO3), a near room temperature ME perovskite, using magnetization and inelastic light scattering measurements as a function of temperature. Temperature-dependent magnetization behavior studied in a wide temperature range of 5–395 K at both field-cooled (FC) and zero-field-cooled (ZFC) conditions using different static magnetic fields confirms the magnetic transition temperature Tc at 220 K. On temperature dependent Raman spectroscopy, no significant changes in Raman spectra were observed at an elevated temperature that can be attributed to the absence of structural phase transition. Instead of expected anharmonic behavior, several librational (rigid rotation) and stretching modes of rigid BO6 units were found to be hardening below Tc, suggesting the significant magnetoelastic coupling contributions to phonon frequencies. The asymmetric stretching mode at 753 cm−1 is found to have larger spin-phonon coupling contribution (λ∼2.93), while the lattice mode at 153 cm−1 and external librational mode at 240 cm−1 had the lowest effect (λ∼0.88).
Highly oriented 0.90[PbZr0.53Ti0.47]0.10[La0.80Sc0.20]O3-δ (PLZTS) thin films deposited on La0.67Sr0.33MnO3 (LSMO) coated MgO (100) substrates were grown by pulsed laser deposition technique. Temperature dependent dielectric measurements on metal-ferroelectric-metal Pt/PLZTS/LSMO thin film capacitors were carried out at several frequencies which exhibit high dielectric constants (450–580) with the diffuse peak around 400 K, and the diffusivity parameter γ was obtained as 1.96 for 100 kHz data. The slim polarization-electric field hysteresis loop was observed with less remanent polarization (∼7–10 μC/cm2) indicating its relaxor behavior. Temperature dependent Raman spectra measured between 80 and 550 K show softening of the symmetric E(LO2) band that disappeared at 300 K, corroborating the tetragonal-cubic phase transition. From the analysis of the measured hysteresis loops, the recovered energy density Ure ∼ 19 J/cm3 with the efficiency η ∼ 66% was estimated, suggesting its possible application in energy density capacitors.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.