Collagen-based films and sponges are widely used as biomaterials. The rate of their biodegradation can be reduced by treating them with different cross-linking agents. The efficiency of different reticulation procedures on thermal stability (measured by differential scanning calorimetry) and susceptibility to bacterial collagenase digestion of the final material (films or sponges) is compared. The chemical agents used on collagen gels or directly on collagen sponges and films were glutaraldehyde (GTA), hexamethylene diisocyanate (HMDC), cyanamide, 1-ethyl-3-(3-dimethyl aminopropyl) carbodiimide (EDC) and the two acyl azide methods (with hydrazine or diphenylphosphorylazide (DPPA)) developed in the authors' laboratory. Under these experimental conditions, collagen stabilization by the different agents increased in the following order: cyanamide < EDC < HMDC < hydrazine < DPPA < GTA. Sponges with the highest thermal stability were obtained by treating collagen gel with 0.5% GTA for 1 h at pH 5.5 (initial T~=75.8°C; after 3 months, Ta=75.6°C). Direct treatment of collagen films with DPPA gave similar thermal stability (Ta=72.6 °C) and collagenase resistance when compared with treatment with 0.6% GTA for 96 h (Td =74.6 °C). It is demonstrated that collagen sponges and films can be prepared with a wide range of thermal stability (49-75.8 °C) and collagenase digestion resistance (10-100%). Recent biocompatibility studies show, however, that DPPA and EDC are the best choices for preparing cross-linked collagen sponges and films.

With the rapid development of tissue engineering and gene therapy, collagen-based biomaterials frequently are used as cell transplant devices. In this study we determined the behavior of mouse fibroblasts cultured for up to 6 weeks in control sponges treated by severe dehydration and used commercially as hemostatic agents and in two sponges (DPPA 2 and 3) crosslinked by diphenylphosphorylazide, a method developed in our laboratory. Growth capacity, biosynthetic and proteolytic activities, and matrix reorganization were followed over time in cultures and compared with similar data for fibroblasts in monolayer culture on plastic and in floating or attached collagen gels. Control sponges with and without seeded mouse fibroblasts showed rapid partial denaturation or contraction, weight loss, and severe calcification (13-18% Ca) after 6 weeks. In contrast, the crosslinked sponges showed only slightly decreased size and weight, and the calcification was inhibited (0.2% Ca) in the presence of cells. Mouse fibroblasts seeded on the crosslinked sponge surface at 50,000-200,000 cells/cm(2) progressively penetrated the matrix and proliferated to give the same constant cell density after 3 weeks (around 600,000 cells/sponge). A specific, two- to threefold decrease in collagen synthesis was observed between 1 and 3 or 6 weeks, due mainly to a decrease in the fraction secreted into the medium (25-30% instead of 45-50%). No collagenase 3 activity was detected in the culture medium under any condition or time whereas 25% gelatinase A was found by gelatin zymography to be in an active form in cultures within sponges as compared with less than 10% in monolayers and more than 50% in floating collagen gel. A small amount of gelatinase B was observed after 1 week in sponge cultures and was completely absent thereafter. These results show that the biosynthetic and proteolytic behavior of mouse fibroblasts cultured in crosslinked collagen scaffolds is different from that in monolayers or in floating collagen gels and more similar to that previously described in attached collagen gels.

No abstract

No abstract

No abstract