The influence of silicon-substituted hydroxyapatite (Si-HAp) on osteogenic differentiation was assessed by biological analysis. Si-HAp was prepared by ultrasonic spray pyrolysis (USSP) technique using various amounts of Si (0, 0.8, and 1.6 mass%). Chemical analysis revealed that Si was incorporated into the hydroxyapatite (HAp) lattice with no other crystalline phase and which caused the change of crystal structure. Biological analyses showed that the Si contents affected the cell proliferation and morphology, suggesting that there is an optimal Si content for cell culture. As for differentiation, alkaline phosphatase activity and osteocalcin production of Si-HAp were higher than those of HAp. Gene expression profiles also revealed that substitution of Si (0.8 mass%) up-regulated the expression levels of osteocalcin and especially Runx2, a master gene for osteoblast development. These results suggest that incorporating Si into the HAp lattice may enhance the bioactivity, particularly during early osteoblast development.
Biodegradableα-tricalcium phosphate (α-TCP) cement based on the chelate-setting mechanism of inositol phosphate (IP6) was developed. This paper examined the effect of the milling time ofα-TCP powder on the material properties of the cement. In addition, biocompatibility of the result cementin vitrousing osteoblasts andin vivousing rabbit models will be studied as well. Theα-TCP powders were ballmilled using ZrO2beads in pure water for various durations up to 270 minutes, with a single-phaseα-TCP obtained at ballmilling for 120 minutes. The resulting cement was mostly composed ofα-TCP phase, and the compressive strength of the cement was8.5±1.1 MPa, which suggested that the cements set with keeping the crystallite phase of starting cement powder. The cell-culture test indicated that the resulting cements were biocompatible materials.In vivostudies showed that the newly formed bones increased with milling time at a slight distance from the cement specimens and grew mature at 24 weeks, and the surface of the cement was resorbed by tartrate-resistant acid phosphatase-(TRAP-)positive osteoclast-like cells until 24 weeks of implantation. The presentα-TCP cement is promising for application as a novel paste-like artificial bone with biodegradability and osteoconductivity.
The hydroxyapatite (HAp) powder preparation process was optimized to fabricate inositol phosphate-HAp (IP6-HAp) cement with enhanced mechanical properties. Starting HAp powders were synthesized via a wet chemical process. The effect of the powder preparation process on the morphology, crystallinity, median particle size, and specific surface area (SSA) of the cement powders was examined, together with the mechanical properties of the resulting cement specimens. The smallest crystallite and median particle sizes, and the highest SSA were obtained from ball-milling of as-synthesized HAp powder under wet conditions and then freeze-drying. IP6-HAp cement fabricated with this powder had a maximum compressive strength of 23.1 ± 2.1 MPa. In vivo histological studies using rabbit models revealed that the IP6-HAp cements were directly in contact with newly formed and host bones. Thus, the present chelate-setting HAp cement is promising for application as a novel paste-like artificial bone.
Novel biodegradable β-tricalcium phosphate (β-TCP) cements with anti-washout properties were created on the basis of chelate-setting mechanism of inositol phosphate (IP6) using β-TCP powders. The β-TCP powders were ball-milled using ZrO₂ beads for 0-6 h in the IP6 solutions with concentrations from 0 to 10,000 ppm. The chelate-setting β-TCP cement with anti-washout property was successfully fabricated by mixing the β-TCP powder ball-milled in 3,000 ppm IP6 solution for 3 h and 2.5 mass% Na₂HPO₄ solution, and compressive strength of the cement was 13.4 ± 0.8 MPa. An in vivo study revealed that the above cement was directly in contact with host and newly formed bones without fibrous tissue layers, and was resorbed by osteoclast-like cells on the surface of the cement. The chelate-setting β-TCP cement with anti-washout property is promising for application as a novel injectable artificial bone with both biodegradability and osteoconductivity.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.