At least 85% of principal procedures using BMP were for off-label applications. With uncertainty regarding the risks of using BMP in certain off-label applications, further research will be needed to better define the appropriate indications. Our study also demonstrates that disparities in the differential rates of BMP use exist in the spine fusion population.
It remains unclear whether adjacent vertebral body fractures are related to the natural progression of osteoporosis or if adjacent fractures are a consequence of augmentation with bone cement. Experimental or computational studies have not completely addressed the biomechanical effects of kyphoplasty on adjacent levels immediately following augmentation. This study presents a validated two-functional spinal unit (FSU) T12-L2 finite element model with a simulated kyphoplasty augmentation in L1 to predict stresses and strains within the bone cement and bone of the treated and adjacent nontreated vertebral bodies. The findings from this multiple-FSU study and a recent retrospective clinical study suggest that changes in stresses and strains in levels adjacent to a kyphoplasty-treated level are minimal. Furthermore, the stress and strain levels found in the treated levels are less than injury tolerance limits of cancellous and cortical bone. Therefore, subsequent adjacent level fractures may be related to the underlying etiology (weakening of the bone) rather than the surgical intervention.
Retrieved rods exhibited corrosion, wear, and fracture, with wear and corrosion mainly located at the interfaces with hooks, screws, or cross-connectors. The mechanisms causing this material loss in situ, as well as what local or systemic responses it may stimulate are of clinical significance and should be studied further.
The resin and processing route have been identified as potential variables influencing the mechanical behavior, and hence the clinical performance, of ultra-high molecular weight polyethylene (UHMWPE) orthopedic components. Researchers have reported that components fabricated from 1900 resin may oxidize to a lesser extent than components fabricated from GUR resin during shelf aging after gamma sterilization in air. Conflicting reports on the oxidation resistance for 1900 raise the question of whether resin or manufacturing method, or an interaction between resin and manufacturing method, influences the mechanical behavior of UHMWPE. We conducted a series of accelerated aging studies (no aging, aging in oxygen or in nitrogen) to systematically examine the influence of resin (GUR or 1900), manufacturing method (bulk compression molding or extrusion), and sterilization method (none, in air, or in nitrogen) on the mechanical behavior of UHMWPE. The small punch testing technique was used to evaluate the mechanical behavior of the materials, and Fourier transform infrared spectroscopy was used to characterize the oxidation in selected samples. Our study showed that the sterilization environment, aging condition, and specimen location (surface or subsurface) significantly affected the mechanical behavior of UHMWPE. Each of the three polyethylenes evaluated seem to degrade according to a similar pathway after artificial aging in oxygen and gamma irradiation in air. The initial ability of the materials to exhibit post-yield strain hardening was significantly compromised by degradation. In general, there were only minor differences in the aging behavior of molded and extruded GUR 1050, whereas the molded 1900 material seemed to degrade slightly faster than either of the 1050 materials.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.