ABSTRACT:The curing kinetics and chemorheology of a low-viscosity laminating system, based on a bisphenol A epoxy resin, an anhydride curing agent, and a heterocyclic amine accelerator, are investigated. The curing kinetics are studied in both dynamic and isothermal conditions by means of differential scanning calorimetry. The steady shear and dynamic viscosity are measured throughout the epoxy/ anhydride cure. The curing kinetics of the thermoset system is described by a modified Kamal kinetic model, accounting for the diffusion-control effect. A chemorheological model that describes the system viscosity as a function of temperature and conversion is proposed. This model is a combination of the Williams-Landel-Ferry equation and a conversion term originally used by Castro and Macosko. A good agreement between the predicted and experimental results is obtained.

No abstract

Hydroxyapatite structures for tissue engineering applications have been produced by hydrothermal (HT) treatment of aragonite in the form of cuttlefish bone at 200 degrees C. Aragonite (CaCO(3)) monoliths were completely transformed into hydroxyapatite after 48 h of HT treatment. The substitution of CO(3) (2-) groups predominantly into the PO(4) (3-) sites of the Ca(10)(PO(4))(6)(OH)(2) structure was suggested by FT-IR spectroscopy and Rietveld structure refinement. The intensity of the nu(3)PO(4) (3-) bands increase, while the intensity of the nu(2)CO(3) (2-) bands decrease with the duration of HT treatment resulting in the formation of carbonate incorporating hydroxyapatite. The SEM micrographs have shown that the interconnected hollow structure with pillars connecting parallel lamellae in cuttlefish bone is maintained after conversion. Specific surface area (S (BET)) and total pore volume increased and mean pore size decreased by HT treatment.

Up till now, chitosan has confirmed its versatile application in skin, cartilage and bone tissue engineering, as well as in drug delivery applications. This study is focused on enzymatic degradation of porous chitosan structures usually designed for mentioned purposes. In vitro degradation was monitored during four weeks of incubation at physiological temperature and in two different media, phosphate buffer saline solution and water.The scaffolds were characterised before and after enzymatic degradation using scanning electron microscopy and infrared spectroscopy with Fourier transformations (FTIR). According to the gravimetric analysis, higher weight loss of chitosan scaffolds was observed in buffered medium with respect to the water. The results implied that the total weight loss obtained in buffer involves physical dissolution of chitosan and lysozyme cleavage of glycoside bond. Importantly, FTIR identification of chitosan scaffolds after enzymatic degradation indicated the absence of lysozyme activity in water, indicating that weight loss is a result of the chitosan dissolution. This finding greatly impacts design of degradation experiments and characterisation of degradation behaviour of chitosan-based materials utilised as implants or drug delivery systems.

No abstract

The permeability of carbon dioxide, oxygen, nitrogen, and air through commercial monolayer and multilayer films, based on polyethylene (PE), biaxially oriented polypropylene (BOPP), and polyamide (PA), used for food packaging is reported. The influence of temperature (from 10 to 60°C) on permeability and DSC characteristics changes was also analyzed. Literature data for gas permeability of the mentioned monofilms are quite variable due to differences in additives, thermal history, and crystallinity. In this work, the highest gas permeability is obtained for PE film at the higher temperature (50–60°C). Laminates exhibit different gas permeation behavior from that of monofilms. Generally, gas solubility coefficient increases at higher temperature (with an exception of PA/PE and BOPPcoex.met/PE), being higher for monofilms in comparison with laminates, while diffusion coefficients are lower for monofilms in comparison with laminates. The temperature dependence of the permeability, diffusivity, and solubility of gases shows two different regions in PE, BOPPcoex/PE (10–40°C and 40–60°C), PA/PE, and BOPPcoex.met (10–30°C and 40–60°C) films. Correlation between activation energies for permeation and diffusion as well as heat of sorption and 17 gas properties is performed. © 2005 Wiley Periodicals, Inc. J Appl Polym Sci 99: 1590–1599, 2006

No abstract

No abstract