Phototherapy with low-level coherent light (laser) has been reported as an analgesic and anti-inflammatory as well as having a positive effect in tissue repair in orthodontics. However, there are few clinical studies using low-level LED therapy (non-coherent light). The aim of the present study was to analyze the pain symptoms after orthodontic tooth movement associated with and not associated with coherent and non-coherent phototherapy. Fifty-five volunteers (mean age = 24.1 ± 8.1 years) were randomly divided into four groups: G1 (control), G2 (placebo), G3 (protocol 1: laser, InGaAlP, 660 nm, 4 J/cm(2), 0.03 W, 25 s), G4 (protocol 2: LED, GaAlAs, 640 nm with 40 nm full-bandwidth at half-maximum, 4 J/cm(2), 0.10 W, 70 s). Separators were used to induce orthodontic pain and the volunteers pain levels were scored with the visual analog scale (VAS) after the separator placement, after the therapy (placebo, laser, or LED), and after 2, 24, 48, 72, 96, and 120 h. The laser group did not have statistically significant results in the reduction of pain level compared to the LED group. The LED group had a significant reduction in pain levels between 2 and 120 h compared to the control and the laser groups. The LED therapy showed a significant reduction in pain sensitivity (an average of 56%), after the orthodontic tooth movement when compared to the control group.
Purpose: The aim of this study was to evaluate the effects of different zirconia surface treatments on the bond strength of two self-adhesive resinous cements (SARC). Methods: Two hundred and eight cylindrical specimens were obtained from Y-TZP zirconia (half with diameter 3.2 mm and half with 4.8 mm). After sintering and polishing, specimens were divided into four groups (n = 26), according to surface treatment: Control (no treatment); Sandblasting (Al 2 O 3 particles); Rocatec (Al 2 O 3 particles, tribochemical silica coating and silane application); Laser (Nd: YAG laser: 20 Hz, 100 mJ, 0.2 J/cm²). The surface roughness (Ra) was evaluated after the surface treatments, and the groups were divided into two subgroups (n = 13), according to the SARC tested: RelyX U200 and Bifix SE. The 2.2-mm cylinders were bonded to 4.8-mm cylinders and stressed until failure under shear using a universal testing machine. Bond strength and Ra were analyzed using ANOVA, and Tukey's test (α = 0.05). Results: Surface treatment was significant (p < 0.0001), but cement type (p = 0.73) was not. Related to roughness, significant differences were found for the treatment type (p < 0.0001), with laser being the treatment with higher Ra values. Conclusions: Nd:YAG laser produced a rougher surface and a higher bond strength compared with sandblasting, silicatization, and control groups.
SUMMARY
Objectives:
This study aimed to evaluate the bonding performance of a universal adhesive used according to self-etching or etch-and-rinse protocols in noncarious cervical lesions (NCCLs) and to compare the two protocols with their respective gold standard techniques.
Methods and Materials:
This randomized, double-blind clinical study enrolled 34 participants who met the inclusion criteria, 29 of whom returned after two years. They received 152 restorations bonded with one of the three adhesives (Scotchbond Universal Adhesive, Adper Single Bond 2, or Clearfil SE Bond) and one of the two bonding techniques tested. The NCCLs were restored with nanocomposite resin (Filtek Supreme). Final contours were done with a fine diamond rotary instrument and polished with rubber points. The restorations were evaluated using the FDI World Dental Federation criteria at baseline (seven days after the restoration procedure), 6, 12, and 24 months. Descriptive statistics, Kruskal-Wallis, Friedman analysis of variance, and least significant difference tests were performed.
Results:
No statistically significant differences were found in esthetics or the functional and biological evaluated criteria among the adhesive systems and techniques.
Conclusions:
The Scotchbond Universal system behaved similarly to the conventional etch-and-rinse or self-etching systems in all the adhesion strategies in the evaluated periods.
This study aimed to evaluate the effect of beers on the bovine enamel microhardness. Fifty rectangular (1 x 3 x 1 mm–height x width x thickness) enamel specimens were obtained from permanent bovine incisors, and divided into five groups (n = 10) according to the treatment employed: Saliva, Coke, Brahma, Heineken, and Budweiser. Microhardness (Knoop) were obtained before; after 5, 30 and 60 min of immersion in each solution. The data were analyzed using repeated two-way ANOVA and Tukey´s test (p<0.05). Coke decreased the microhardness in all immersion times, and Heineken, showed low values after 60 minutes. Beers tested have low potential to cause enamel erosion when compared to Coke.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.