This work presents the results of the study of the physical, chemical, mineralogical and pozzolanic properties of the altered volcanic tuffs (AVT) that lie in the Los Frailes caldera, south of the Iberian Peninsula, and demonstrates their qualities as pozzolans for the manufacturing of mortars and pozzolanic cements of high mechanical strength. The main objective of this research is to show to what extent the AVTs can replace portland cement (PC) in mortars, with standardised proportions of 75:25% and 70:30% (PC-AVT). To achieve these objectives, three AVT samples were studied by a petrographic analysis of thin section (PATS), DRX, FRX and MEB. The pozzolanic properties were determined by three methods: electrical conductivity (ECT), chemical pozzolanicity tests (CPT) at 8 and 15 days and mechanical strength tests (MS) of the specimens at 2, 7, 28 and 90 days. Studies of a PATS, DRX, FRX and MEB showed that the AVT samples’ constitutions are complex where smectite (montmorillonite), mordenite, quartz, halloysite, illite, kaolinite, volcanic glass and lithic fragments coexist. The results of the ECT and CPT tests confirmed the pozzolanic properties of the samples analysed and proved an increase in mechanical strength from 2 to 90 days of testing.

This work deals with anomalous concentrations of natural mordenite in the southeast of Spain. The X-ray diffraction (XRD) and scanning electron microscopy (SEM) studies evidenced that the samples contain mainly monomineral zeolitic phase of mordenite (70% to 74%), usually accompanied by smectite (montmorillonite), the principal component of bentonite. A study of the applicability of these zeolites is presented to establish the potential use as pozzolanic cements. For comparative purposes, synthetic commercial mordenite is also characterized and tested. The initial mixtures were prepared using cement and mordenite at a 75:25 ratio. Chemical analysis and a pozzolanicity test showed the high pozzolanic character. These mixtures were further added to sand and water, yielding the cement specimens to be used as concrete. Mechanical test results showed that the mechanical compression at 7 and 28 days fall into the range of 19.23 to 43.05 MegaPascals (MPa) for the cement specimens built with natural mordenites. The obtained results fall in the same range of cement specimens prepared with natural clinoptilolite, using mixtures within the European requirement for commercial concretes. Thus, these results and the low cost of natural mordenite of San José de los Escullos deposit supports the potential use of natural mordenite as pozzolanic cement.

This work aims to study the relationship between the compression resistance and velocity from ultrasonic pulses in samples of mortars with 25% of pozzolanic content. Pozzolanic cement is a low-priced sustainable material that can reduce costs and CO2 emissions that are produced in the manufacturing of cement from the calcination of calcium carbonate. Using ultrasonic pulse velocity (UPV) to estimate the compressive resistance of mortars with pozzolanic content reduces costs when evaluating the quality of structures built with this material since it is not required to perform an unconfined compression test. The objective of this study is to establish a correlation in order to estimate the compression resistance of this material from its ultrasonic pulse velocity. For this purpose, we studied a total of 16 cement samples, including those with additions of pozzolanic content with different compositions and a sample without any additions. The results obtained show the mentioned correlation, which establishes a basis for research with a higher number of samples to ascertain if it holds true at greater curing ages.

In recent decades, large amounts of construction and demolition waste (CDW) have been generated and accumulated throughout Europe, which is a challenge to manage and control nowadays. This work shows the results of a study carried out with samples of ceramic recycled aggregates (CRAs) and recycled concrete aggregates (RCAs) mixed with cement (C) in mortars. The main objective of this research is to demonstrate how, by adding CRAs and RCAs to a mixture of cement and natural aggregate (NA), it is possible to develop a high-strength mortar and achieve the best mixing ratio. To achieve these objectives, the characterization of the samples was initially carried out such as XRF, XRD and SEM. Next, tests were carried out on the products obtained, such as the consistency of the fresh mortar and the density of the specimens. Finally, a study of mechanical compressive strength was performed at 7, 28 and 200 days. The results show that although both CRAs and RCAs negatively affect the curing process of the specimens, it is possible to develop mortars with compressive strengths greater than 20 MPa. An obvious increase in mechanical compressive strengths was seen between 7 and 200 days of analysis. The results achieved in this research could be an important guide for the management of CDWs by local industries, thus favouring the development of the circular economy.

The eruption of the Cumbre Vieja volcano on 19 September 2021, resulted in the deposition of large quantities of volcanic ash (VA), causing a great impact on the citizens. This work aims to study the properties of this volcanic ash as pozzolanic raw materials to establish their potential use in the development of sustainable cement. Results of chemical and technical characterization are presented. To achieve this goal, Ordinary Portland Cement (OPC) was replaced with standardized percentages of OPC/VA: 10, 25, and 40%. Characterization studies were carried out using chemical analysis of X-ray fluorescence (XRF), chemical quality analysis (QCA), pozzolanicity test (PT) at 8 and 15 days, as well as determining the mechanical strength (MS) at 7, 28, and 90 days. The results obtained by XRF and QCA established that the chemical composition of the VA corresponds to that of the natural pozzolan typical of pyroclastic genesis. The PT test showed that the analyzed samples have a marked pozzolanic nature, both at 8 and 15 days, showing a significant increase in their hydraulic reactivity. Likewise, the MS tests confirmed a continuous increase in mechanical compressive strength, which increased significantly from 7 to 90 days of curing, reaching more than 58 MPa. On the other hand, mechanical tests showed that the three types of dosages used OPC/VA: 10, 25, and 40% were equally effective, with OPC/VA formulations: 10–25% being the most effective. The results obtained in this research could be used by local industries as a guide for the correct use of the volcanic materials of this island, both for the manufacture of construction materials, such as aggregates, and to produce pozzolanic cement with low CO2 emissions, thus having a positive impact on the environment. Finally, the great natural availability of natural VAs in the surrounding areas of La Palma could cover part of the needs for materials used in the construction and restoration of houses and infrastructures damaged during the volcanic eruption.

The speed at which climate change is happening is leading to a demand for new pozzolanic materials that improve the quality of cements and, at the same time, limit the emission of greenhouse gases into the atmosphere. The main objective of this work is the detailed characterization of an ignimbrite sample (IGNS) to demonstrate its effectiveness as a natural pozzolan. To meet this objective, a series of tests were carried out. In the first stage, mineral and chemical analyses were performed, such as petrographic analysis by thin section (TSP), X-ray diffraction (XRD), oriented aggregate (OA), scanning electron microscopy (SEM) and X-ray fluorescence (XRF). In the second stage, the following technical tests were carried out: chemical quality analysis (QCA), pozzolanicity test (PT) and mechanical compressive strength (MS) at 7, 28 and 90 days, using mortar specimens with ignimbrite/cement formulation (IGNS/PC): 10, 25 and 40% to establish the pozzolanic nature of the ignimbrite. The results of the mineral and chemical analyses showed that the sample has a complex mineralogical constitution, consisting of biotite mica, potassium feldspar, plagioclase, smectite (montmorillonite), quartz, volcanic glass, iron, titanium and manganese oxides, chlorite and chlorapatite. On the other hand, the technological tests revealed the pozzolanic nature of the sample, as well as visible increases in the mechanical compressive strengths in the three proportions, the most effective being IGNS/PC:10% and IGNS/PC:25% at 7, 28 and 90 days of setting. The results obtained could be applied in the formulation of new pozzolanic cements with ignimbrite as a natural pozzolanic aggregate.

Metropolitan construction and demolition waste (CDW) is currently an important source of recycled materials that, despite having completed their useful life cycle, can be reincorporated into the circular economy process (CEP); however, the recycling process is very selective, and waste material is not always fully satisfactory due to the intrinsic nature of the waste. This work aims to demonstrate and establish how to increase the effectiveness of the construction and demolition waste in more resistant mortars, by mixing it with zeolitised cinerite tuff (ZCT) at varying normalised proportions. To attain the objectives of this research, a series of tests were done: First, a chemical, physical and mineralogical characterisation of the CDW and the ZCT through XRF, XRD, SEM and granulometric methods. Second, a technological test was made to determine the mechanical strength at 7, 28 and 90 days of specimens made with Portland cement (PC) and mixtures of PC/CDW, PC/ZCT, and PC/CDW-ZCT. The results obtained through the characterisation methods showed that the sample of construction and demolition waste consisted of the main phase made of portlandite and tobermorite, and by a secondary phase consisting of quartz, ettringite and calcite; whereas the ZCT has a main phase of mordenite and a secondary phase of smectite (montmorillonite), amorphous materials consisting of devitrified volcanic glass, quartz and plagioclase. Mechanical strength tests established that specimens made with PC/CDW mixtures have very discreet compressive strength values up to 44 MPa at 90 days, whereas specimens made with PC/ZCT mixtures achieved a remarkably high mechanical strength consisting of 68.5 MPa. However, the most interesting conclusion in this research is the good result obtained in mechanical strength of the specimens made up of mixtures of PC/CDW-ZCT, which increased from 52.5 to 62 MPa at 90 days of curing; this fact establishes the positive influence of ZCT on waste in the mortar mixtures, which permits the authors to establish that the objective of the work has been fulfilled. Finally, it can be argued that the results obtained in this research could contribute to more effective use of construction and demolition waste in metropolitan areas.

University students face situations throughout their careers that are sometimes difficult to overcome due to their lack of experience or preparation. Mentoring programs in university education have been proven to be a great accompaniment tool to solve these difficulties in addition to helping students’ personal and professional development. Our study aimed to show the complete mentoring process that accompanies students in the most crucial stages of their university education at the School of Mines and Energy of Universidad Politécnica de Madrid. Three stages of interest were identified in which mentoring projects have been implemented through training activities at the Unit of Social Entrepreneurship, Ethics and Values in Engineering (UESEVI). At the beginning of their studies, two welcome actions are offered: Mentor and Monitor projects that provide administrative and academic support; during the development of their studies, the Mentoring with Energy project offers professional tutoring that helps students in their incorporation into the labor market and provides them with tools to select a specialty; and in the last stage, professional accompaniment is provided by the Gray Angels project that helps students to develop their future careers. The activities of UESEVI are a strategy in our School to guarantee the development of soft skills and compliance with quality education processes. The usefulness of these programs can be measured through the participation and interest of the students. A positive evolution of these projects has been observed over the years. They have been growing according to the demand and needs detected in the successive evaluations of the programs.