In situ three-dimensional (3-D) X-ray diffraction experiments have been performed at a synchrotron source on low-alloyed multiphase TRIP steels containing 0.25 wt.% Si and 0.44 wt.% Al and produced with different bainitic holding times, in order to assess the influence of the bainitic transformation on the thermal stability of individual austenite grains with respect to their martensitic transformation. A detailed characterization of the austenite grain volume distribution at room temperature was performed as a function of the prior bainitic holding time. In addition, the martensitic transformation behaviour of individual metastable grains was studied in situ during cooling to a temperature of 100 K. Both the carbon content and the grain volume play a key role in the stability of the austenite grains below 15 lm 3 , while the carbon content exerts the dominant effect in the stability of the bigger grains. Measurements also suggest that the tetragonality of the thermally formed martensite is suppressed.
Using high-resolution neutron diffraction measurements for Mn-rich hexagonal Mn-Fe-P-Si compounds, we show that the substitution of Mn for Fe on the 3f sites results in a linear decrease of the Fe/Mn(3f ) magnetic moments, while the Mn(3g) magnetic moments remain constant. With increasing temperature, the Mn(3g) magnetic moments show almost no change, while the Fe/Mn(3f ) moments decrease quickly when the transition temperature is approached. The reduction of the magnetic moments at the transition temperature and in the high-temperature range is discussed based on changes in interatomic distances and lattice parameters and high-temperature magnetic-susceptibility measurement.
The stability of the retained austenite has been studied in situ in low-alloyed transformation-induced-plasticity (TRIP) steels using high-energy X-ray diffraction during tensile tests at variable temperatures down to 153 K. A detailed powder diffraction analysis has been performed to probe the austenite-to-martensite transformation by characterizing the evolution of the phase fraction, load partitioning and texture of the constituent phases simultaneously. Our results show that at lower temperatures the mechanically induced austenite transformation is significantly enhanced and extends over a wider deformation range, resulting in a higher elongation at fracture. Low carbon content grains transform first, leading to an initial increase in average carbon concentration of the remaining austenite. Later the carbon content saturates while the austenite still continues to transform. In the elastic regime the probed {h k l} planes develop different strains reflecting the elastic anisotropy of the constituent phases. The observed texture evolution indicates that the austenite grains oriented with the {2 0 0} plane along the loading direction are transformed preferentially as they show the highest resolved shear stress. For increasing degrees of plastic deformation the combined preferential transformation and grain rotation results in the standard deformation texture for austenite with the {1 1 1} component along the loading direction. The mechanical stability of retained austenite in TRIP steel is found to be a complex interplay between carbon concentration in the austenite, grain orientation, load partitioning and temperature.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.