Thin films of tin doped zinc oxide (ZnO: Sn) with thickness 300 ± 30 nm prepared by spray pyrolysis method at substrate temperatures of 400°C. The structure, surface morphological and optical properties were studied, for Two weight ratios of doping (2 and 4) wt %. The results of X-Ray measurements showed that all deposit samples have a polycrystalline pattern with hexagonal wurtzite type structure. The films crystallites were oriented along (002) plane. The morphology measurements obtained by scanning electron microscope (SEM) showed that there is a change in the surface texture by the increasing of tin weight ratios with the rate of porosity of the surface when treating with 4wt %. The measurement of Atomic force microscopy (AFM) revealed nano particles sized and the roughness of the surface decrease to increase deflection, while optical measurements showed a decrease The energy gap of the models that are expected in the undoped samples.

Fe 2 O 3 thin films that doped by NiO were obtained on glass substrates by the chemical spray pyrolysis technique, and annealed at 450 ºC and 500 ºC. The effect of annealing on optical properties was studied by recording the absorbance spectra using UV-Visible spectrophotometer. The refractive index decreases with increasing annealing temperature, such as an optical band gap that decreases from 2.68 eV before annealing to 2.58 eV after annealing of 500 ºC. Absorption coefficient and extinction coefficient increase with increasing annealing temperature.

No abstract

Spray pyrolysis method that used to prepare Cu:NiO thin films onto glass substrate with various annealing temperature. Spectral transmittance of prepared thin films determined by UV-Visible spectrophotometer in the range of (380-900) nm. The transmittance decreased with increasing annealing temperature. While the absorption coefficient and extinction coefficient increased with increasing annealing temperature. Energy gap decreased from 2.9 eV before annealing to 2.78 eV after 500 ºC annealing temperature.

No abstract