Biphenyl was grafted on rigid-rod aromatic poly(p-phenylenesulfonic acids) (IEC ∼ 8 mequiv g −1 ) to generate cross-linkable polyelectrolytes. Cross-linking conditions and film properties before and after cross-linking were studied. Films equilibrated between 20 and 30% relative humidity (RH) had tensile moduli of 2 to 1 GPa and broke at 5 to 9% elongation. The moduli decreased as RH increased and dropped drastically at high humidity if the films were not cross-linked. Grafted films had conductivities at 80 °C 4−5 times that of Nafion NR-212 over the whole relative humidity range even after cross-linking. The sample reported in detail here had a conductivity of 0.10 S cm −1 at 120 °C and 30% RH. As is usual for this class of materials, even after the loss of 24% of starting sulfonic acid groups by grafting and cross-linking, ionic conductivity was high at low humidity. A membrane electrode assembly (MEA) prepared with this rigid-rod poly(phenylenesulfonic acid) proton exchange membrane and tested in a fuel cell exhibited performance and properties similar to those of Nafion NR-212 films. The power density was ∼95% of that of the Nafion MEA over the operating range in spite of relatively high hydrogen crossover due to the presence of nanocracks in the membrane.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.