Atomic layer deposition (ALD) of Al2O3 on electrospun poly(vinyl alcohol) microfiber templates is demonstrated as an effective and robust strategy by which to fabricate long and uniform metal-oxide microtubes. The wall thickness is shown to be precisely controlled within a molecular layer or so by adjusting the number of ALD cycles utilized. By judicious selection of the electrospinning and ALD parameters, designer tubes of various sizes and inorganic materials can be synthesized.
Atomic layer deposition (ALD) of aluminum oxide on nonwoven polypropylene and woven cotton fabric materials can be used to transform and control fiber surface wetting properties. Infrared analysis shows that ALD can produce a uniform coating throughout the nonwoven polypropylene fiber matrix, and the amount of coating can be controlled by the number of ALD cycles. Upon coating by ALD aluminum oxide, nonwetting hydrophobic polypropylene fibers transition to either a metastable hydrophobic or a fully wetting hydrophilic state, consistent with well-known Cassie-Baxter and Wenzel models of surface wetting of roughened surfaces. The observed nonwetting/wetting transition depends on ALD process variables such as the number of ALD coating cycles and deposition temperature. Cotton fabrics coated with ALD aluminum oxide at moderate temperatures were also observed to transition from a natural wetting state to a metastable hydrophobic state and back to wetting depending on the number of ALD cycles. The transitions on cotton appear to be less sensitive to deposition temperature. The results provide insight into the effect of ALD film growth mechanisms on hydrophobic and hydrophilic polymers and fibrous structures. The ability to adjust and control surface energy, surface reactivity, and wettability of polymer and natural fiber systems using atomic layer deposition may enable a wide range of new applications for functional fiber-based systems.
Nucleation and subsequent growth of aluminum oxide by atomic layer deposition (ALD) on polypropylene fiber substrates is strongly dependent on processing temperature and polymer backbone structure. Deposition on cellulose cotton, which contains ample hydroxyl sites for ALD nucleation and growth on the polymer backbone, readily produces a uniform and conformal coating. However, similar ALD processing on polypropylene, which contains no readily available active sites for growth initiation, results in a graded and intermixed polymer/inorganic interface layer. The structure of the polymer/inorganic layer depends strongly on the process temperature, where lower temperature (60 degrees C) produced a more abrupt transition. Cross-sectional transmission electron microscopy images of polypropylene fibers coated at higher temperature (90 degrees C) show that non-coalesced particles form in the near-surface region of the polymer, and the particles grow in size and coalesce into a film as the number of ALD cycles increases. Quartz crystal microbalance analysis on polypropylene films confirms enhanced mass uptake at higher processing temperatures, and X-ray photoelectron spectroscopy data also confirm heterogeneous mixing between the aluminum oxide and the polypropylene during deposition at higher temperatures. The strong temperature dependence of film nucleation and subsurface growth is ascribed to a relatively large increase in bulk species diffusivity that occurs upon the temperature-driven free volume expansion of the polypropylene. These results provide helpful insight into mechanisms for controlled organic/inorganic thin film and fiber materials integration.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.