The wood panel industry is constantly growing, being necessary the innovation in technologies and raw materials to improve the quality of the final product. Considering the shortage and pressure to decrease the dependence of wood, there is an interest in other renewable materials such as agricultural wastes. Among these wastes, coffee parchment is one which deserves notoriety. An alternative use for coffee parchment could be for production of particleboard in association with wood particles. This study aimed to evaluate the feasibility of using coffee parchment for production of particleboard. The following percentages of wastes were used: 0, 10, 20, 30, 40 and 50% in association to eucalyptus wood. The panels were produced with 8% of urea formaldehyde (based on dry weight of particles). The pressing cycle consisted by: pre-pressing of 0.5 MPa for 10 minutes followed by pressing of 4.0 MPa, and temperature of 160° C for 15 minutes. The compaction ratio of particleboards produced using higher quantities of parchment improved the physical properties. The properties of Water Absorption (2 and 24 h) and Thickness Swelling (2 h) decreased with increasing percentage of coffee parchment. The Thickness Swelling (24 h) showed not significant effect with an increase of coffee waste. The Modulus of Elasticity for coffee parchment particleboards was in the range 646.49 ± 112.65 to 402.03 ± 66.24 MPa, while the Modulus of Rupture ranged from 8.18 ± 1.39 to 4.45 ± 0.75 MPa. The results showed that 10% of coffee parchment could be added for production of particleboards.Index terms: Agricultural waste; lignocellulosic material; renewable material. RESUMOA indústria de painéis de madeira vem em constante crescimento, sendo necessária a inovação em tecnologias e matéria-prima para melhorar a qualidade do produto final. Considerando a escassez e pressão na diminuição da dependência por madeira, existe um interesse em outros materiais renováveis, como os resíduos agrícolas. Entre esses resíduos, o pergaminho de café merece destaque. Uma alternativa para utilização do pergaminho de café poderia ser na produção de particulados, em associação com partículas de madeira. O objetivo deste trabalho foi avaliar a viabilidade de utilização do pergaminho de café para produção de aglomerados. As porcentagens de resíduo utilizadas foram: 0, 10, 20, 30, 40 e 50% em associação com madeira de eucalipto. Os painéis foram produzidos com 8% de uréia-formaldeído (base massa seca de partículas). O ciclo de prensagem consistiu de: pré-prensagem de 0,5 MPa por 10 minutos, seguido por prensagem de 4,0 MPa e temperatura de 160° C por 15 minutos. A razão de compactação dos painéis produzidos com maiores quantidades de pergaminho melhorou as propriedades físicas. As propriedades de absorção de água (2 e 24 h) e inchamento em espessura (2 h) diminuíram com o aumento da porcentagem de pergaminho de café. O inchamento em espessura (24 h) não apresentou diferenças significativas com o aumento de resíduo de café. O Módulo de Elasticidade dos painéis vari...
RESUMONeste trabalho objetivou-se avaliar a influência da incorporação de casca de café nas propriedades físico-mecânicas de painéis aglomerados produzidos com Eucalyptus urophylla S.T. Blake. Os painéis foram produzidos com incorporação de 25, 50 e 75% de casca de café, em três teores da resina fenol-formaldeído (6, 9 e 12%) e 1% de parafina. A densidade nominal dos painéis foi de 0,7 g/cm³ e o ciclo de prensagem compreendeu uma pressão de 3,92 MPa e temperatura de 180ºC por 8 minutos. Pelos resultados obtidos foi possível observar que: as propriedades físicas dos painéis aglomerados apresentam relação linear decrescente com o aumento do teor de resina, e crescente com a porcentagem de casca de café, apresentando maiores valores de absorção de água e inchamento em espessura. As propriedades mecânicas apresentam relação linear crescente com o aumento do teor de resina, e decrescente com a porcentagem de associação de casca de café. Do modo que a pesquisa foi conduzida, a incorporação da casca de café prejudica a qualidade dos painéis produzidos.Termos para indexação: Casca-de-café, aglomerado, Eucalyptus urophylla. ABSTRACTThe objective of this study was to evaluate the influence of the incorporation of Coffee husks in the production of particleboard with Eucalyptus urophylla S.T. Blake. The panels were produced incorporating 25%, 50%, and 75% of Coffee husks at three levels of resin phenol-formaldehyde (6, 9 and 12%) and 1% of paraffin. The nominal density of the panels was 0.7 g/cm³ and the cycle of pressing consisted in a pressure of 3.92 MPa under a temperature of 180°C for 8 minutes. By the results it was possible to observe that the physical properties of the particleboard have a linear relationship decreasing with the increase in the level of resin, and increasing with the increase in the percentage of coffee husks, showing higher values of water absorption and thickness swelling. The mechanical properties show a linear relationship growing with the increase of resin level, and decreasing with a reduction the percentage of coffee husk association. The way that the search was conducted, the incorporation of the Coffee husks harms the quality of the panels produced.
RESUMOEste trabalho teve como objetivo avaliar o efeito da associação de bagaço de cana, tipo e teor de adesivo nas propriedades físico-mecânicas de painéis aglomerados com madeira de Pinus spp. O delineamento experimental se constituiu de um esquema fatorial 3x2x3, sendo três porcentagens de substituição de madeira de pinus por bagaço de cana -25, 50 e 75%; dois tipos de adesivos -fenol-formaldeído (FF) e ureia-formaldeído (UF); e três teores de adesivo -6, 9 e 12%. O ciclo de prensagem utilizado foi de pressão de 40 kgf/cm², temperatura de 160ºC para UF e de 180ºC para FF, e por um tempo de 8 minutos. Mediante os resultados pode-se concluir que: 1) Para a porcentagem de associação de bagaço de cana, nas propriedades em que foi observado efeito significativo, a tendência foi de diminuição da qualidade dos painéis à medida que se aumenta a quantidade de associação de bagaço de cana; 2) O adesivo UF se mostrou estatisticamente igual ou superior a FF em todas as propriedades avaliadas; 3) Os teores de adesivo apresentaram efeito significativo para todas as propriedades analisadas, sendo que, com exceção da propriedade ligação interna, em todas as outras propriedades o teor de 12% foi estatisticamente superior a 6%, e ainda igual ou superior a 9%. Palavras-chave: aglomerados; bagaço de cana; pinus; tipo e teores de adesivo. ABSTRACTThis study aimed to evaluate the association effect of sugar cane bagasse, type and levels of adhesive in the physical-mechanical properties of particleboards with Pinus spp. wood. The experimental design consisted of a 3x2x3 factorial scheme, with three percentages of substitution pine wood by sugar cane bagasse -25, 50 and 75%; two types of adhesives -phenol-formaldehyde (PF) and urea-formaldehyde (UF); and three levels of adhesive -6, 9 and 12%. The cycle of pressing used was 40kgf/cm² pressure, temperature of 160ºC for UF and 180ºC for PF, and for a time of 8 minutes. From the results, it is concluded that: 1) For the percentage of sugar cane bagasse association, in the properties where significant effect was observed, the trend was decrease in panel quality as the amount of sugar cane bagasse increases; 2) The UF adhesive was statistically equal or greater than PF in all evaluated properties; 3) The levels of adhesive showed significant effects for all properties; Except for internal bond property, in all other properties the level of 12% was statistically superior to 6%, and equal or greater than 9%.
RESUMO:O trabalho teve como objetivo avaliar o potencial de clones de Eucalyptus urophylla para produção de painéis aglomerados homogêneos de baixa densidade. Foram avaliados seis clones de Eucalyptus urophylla com 94 meses de idade, plantados no município de Paracatu-MG, sendo utilizada como parâmetro de comparação a madeira de Pinus oocarpa. Para cada clone de Eucalyptus urophylla e também para o Pinus oocarpa foram produzidos seis painéis com o adesivo uréia-formaldeído no teor de 6%, densidade nominal de 0,60 g/cm³, pressão específica de 40kgf/cm², temperatura de 160ºC e tempo de 8 minutos. Os clones de Eucalyptus urophylla apresentaram potencial para produção de painéis aglomerados convencionais de baixa densidade. Os clones 62 e 28 obtiveram os melhores resultados em todas as propriedades físico-mecânicas avaliadas, apresentando propriedades iguais ou superiores as obtidas para os painéis produzidos com a madeira de Pinus oocarpa. QUALITY OF HOMOGENEOUS PARTICLEBOARD PRODUCED WITH Eucalyptus urophylla CLONE WOOD ABSTRACT: The study aimed to evaluate the potential of Eucalyptus urophylla clones to produce homogeneous particleboard of low-density. Six clones of Eucalyptus urophylla were evaluated, at 94 months of age and planted in Paracatu-MG. Pinus oocarpa wood was used as a reference. For each Eucalyptus urophylla clone and also for Pinus oocarpa, six panels were produced with
RESUMO Há necessidade de diversificação do setor de painéis reconstituídos por meio da introdução de resíduos lignocelulósicos no processo produtivo. Além de agregar valor a materiais residuais, isso poderá contribuir para o aumento da produção industrial de painéis sem a necessidade de implantação de novos plantios florestais. O objetivo desse trabalho foi avaliar as propriedades físicas e mecânicas de painéis aglomerados de baixa densidade produzidos com diferentes quantidades de bagaço de cana-de-açúcar e madeira de Eucalyptus grandis. Os painéis foram produzidos com o adesivo ureia-formaldeído na proporção de 10% em relação à massa do painel. Na produção dos painéis foi utilizada pré-prensagem a 0,5 MPa durante 10 minutos seguida de 4,0 MPa e 160°C durante 15 minutos. As porcentagens de resíduo utilizadas foram: 0, 20, 40 e 60% em associação com madeira de eucalipto. Para a avaliação da qualidade das chapas foram realizados ensaios físicos e mecânicos. O experimento foi arranjado em delineamento inteiramente casualizado, com três repetições. Para avaliação dos dados foi utilizada análise regressão linear simples. Constatou-se que a absorção de água não foi afetada pela inserção de bagaço de cana no painel, enquanto para inchamento em espessura, o aumento da proporção deste resíduo resultou em acréscimo nesta propriedade. As propriedades mecânicas foram afetadas negativamente com a inserção do bagaço de cana-de-açúcar. Os painéis produzidos com o bagaço de cana-de-açúcar e madeira não se adequaram à norma CS 236-66 no que se refere ao módulo de elasticidade na flexão estática. Os resultados demonstraram que até 26% de bagaço de cana-de-açúcar poderia ser utilizado em associação com a madeira de eucalipto na produção de painéis aglomerados de baixa densidade. Palavras-chave: propriedades físico-mecânicas, material lignocelulósico, aproveitamento de resíduo. Valorization of sugarcane bagasse for production of low density particleboards ABSTRACT It's necessary to diversify the reconstituted panels sector by introducing lignocellulosic wastes in the production process. In addition to adding value to wastes materials, this may contribute to the increase the industrial production of panels eliminating the need of new forest plantations. The aim of this study was to evaluate the physical and the mechanical properties of low density particleboards produced with different amounts of sugarcane bagasse and Eucalyptus grandis wood. The panels were produced with 10% of urea formaldehyde adhesive (based on dry weight of particles). The pressing cycle consisted by: pre-pressing of 0.5 MPa during 10 minutes followed by pressing of 4.0 MPa and temperature at 160°C for 15 minutes. The following percentages of wastes were used: 0, 20, 40 and 60% in association to eucalypt wood. For the evaluation of the quality of the panels, physical and mechanical tests were performed. The experiment was carried out according a completely randomized design with three replications. For data analysis, simple linear regression was used. It was ve...
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
334 Leonard St
Brooklyn, NY 11211
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.