This paper reports data for back-illuminated planar n-on-p HgCdTe electroninitiated avalanche photodiode (e-APD) 4 · 4 arrays with large unit cells (250 · 250 lm 2 ). The arrays were fabricated from p-type HgCdTe films grown by liquid phase epitaxy (LPE) on CdZnTe substrates. The arrays were bumpmounted to fanout boards and characterized in the back-illuminated mode. Gain increased exponentially with reverse bias voltage, and the gain versus bias curves were quite uniform from element to element. The maximum gain measured was 648 at -11.7 V for a cutoff wavelength of 4.06 lm at 160 K. For the same reverse-bias voltage, the gains measured at 160 K for elements with two different cutoff wavelengths (3.54 lm and 4.06 lm at 160 K) show an exponential increase with increasing cutoff wavelength, in agreement with BeckÕs empirical model for gain versus voltage and cutoff wavelength in HgCdTe e-APDs. Spot scan data show that both the V = 0 response and the gain at V = -5.0 V are spatially uniform over the large junction area. To the best of our knowledge, these are the first spot scan data for avalanche gain ever reported for HgCdTe e-APDs. Capacitance versus voltage data are consistent with an ideal abrupt junction having a donor concentration equal to the indium concentration in the LPE film.
This article reports new characterization data for large-area (250 lm · 250 lm) back-illuminated planar n-on-p HgCdTe electron-initiated avalanche photodiodes (e-APDs). These e-APDs were fabricated in p-type HgCdTe films grown by liquid-phase epitaxy (LPE) on CdZnTe substrates. We previously reported that these arrays exhibit gain that increases exponentially with reverse bias voltage, with gain-versus-bias curves that are quite uniform from element to element, and with a maximum gain of 648 at -11.7 V at 160 K for a cutoff wavelength of 4.06 lm. Here we report new data on these planar e-APDs. Data from a third LPE film with a longer cutoff wavelength (4.29 lm at 160 K) supports the exponential dependence of gain on cutoff wavelength, for the same bias voltage, that we reported for the first two films (with cutoffs of 3.54 lm and 4.06 lm at 160 K), in agreement with BeckÕs empirical model for gain versus voltage and cutoff wavelength in HgCdTe e-APDs. Our lowest gain-normalized current density at 80 K and zero field-of-view is 0.3 lA/cm 2 at -10.0 V for a cutoff of 4.23 lm at 80 K. We report data for the temperature dependence of gain over 80 K to 200 K. We report, for the first time, the dependence of measured gain on junction area for widely spaced circular diodes with radii of 20 lm to 175 lm. We interpret the variation of measured gain with junction area in terms of an edge-enhanced electric field, and fit the data with a two-gain model having a lower interior gain and a higher edge gain. We report data for the excess noise factor F(M) near unity for gains up to 150 at 196 K. We describe the abrupt breakdown phenomenon seen in most of our devices at high reverse bias.
The effects of dislocations on very-long-wavelength infrared (VLWIR) HgCdTe photodiodes (cutoff wavelength >14 lm at 40 K) have been determined experimentally and analyzed. The photodiodes are in the back-illuminated configuration, fabricated from HgCdTe p-on-n double-layer heterostructure (DLHJ) films grown at BAE Systems by liquid phase epitaxy (LPE) onto lattice-matched (111) CdZnTe substrates. Arrays were hybridized to silicon ROICs to form focal plane arrays (FPAs). After characterization for dark current and response, the arrays were dehybridized and stripped of their metals and passivation layers. Dislocations were revealed using a Hä hnert and Schenk (H&S) etch. Pixel traceability was maintained throughout the analysis, permitting one-to-one correlation between photodiode performance and dislocation density measured within that photodiode. We found that response and dark current were correlated to etch pit density (EPD), which we assumed to be equal to dislocation density. Our results support earlier dislocation studies on larger-bandgap HgCdTe, which showed response was only weakly impacted by EPD, while dark current was strongly affected by EPD. Measured EPD values ranged from low 10 5 to low 10 7 cm -2 . Potential causes for this range in EPD are discussed.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.