Conductive polymer, polypyrrole (PPy), was synthesized by chemical oxidative polymerization technique for a period of four hours at room temperature using pyrrole monomer (mPPy) in aqueous solution. Different oxidants such as ferric chloride (FeCl 3 ) and ammonium persulphate (N 2 H 8 S 2 O 8 ) and surfactant sodium dodecyl sulphate (C 12 H 25 NaO 4 S) were used. The produced PPy samples were characterized by using different techniques such as the electrical resistivity by four probe technique, thermogravimetry analysis (TGA), differential scanning calorimetry (DSC), Fourier transform infrared (FTIR) spectroscopy, X-ray diffraction (XRD), and scanning electron microscopy (SEM). The performance of the oxidants has been investigated and compared. It was found that both oxidants, FeCl 3 and N 2 H 8 S 2 O 8 , have decreased electrical resistivity as a function of temperature, which means increased conductivity. However, FeCl 3 has achieved better performance than N 2 H 8 S 2 O 8 , where it has achieved a lower resistivity of about 60 ohms at room temperature, which indicates higher conductivity of PPy samples with FeCl 3 as an oxidant. Similarly, further investigation of FeCl 3 oxidant has been conducted by varying its concentration, and its influence on the final properties was reported. It has been observed that the morphology of PPy samples has a significant influence on the conductivity. It was found that 0.1 M and 0.05 M concentrations of FeCl 3 oxidant and monomer, respectively, have achieved better thermal stability, which is FeCl 3 /mPPy ratio of 2 as an optimum value. FTIR and XRD results confirmed the structural formation of polypyrrole from pyrrole monomer during the synthesizing process.
In this study, linear low density polyethylene (LLDPE) was grafted and crosslinked by reactive extrusion melt compounding using different silane concentration with and without the presence of montmorillonite (MMT) nanoclay.The effects of different silane concentration and the addition of nanoclay filler on the degree of crosslinking, mechanical, thermal, rheological, and morphological properties were investigated and reported. Gel content results for all
Polypropylene montmorillonite (MMT) nanocomposites were prepared by melt blending using two different organoclays modified with imidazolium and alkylammonium surfactants. The imidazolium and ammonium modified organoclays were characterized by the FTIR and SEM analysis. The effect of organic clay (MMT) on the physical properties of polypropylene was evaluated, thermal and rheological properties with different filler weight percentage. Differential scanning calorimetric results showed that imidazolium modified clay (IMMT) exhibits low melting temperature compared to the ammonium modified clay (AMMT). The crystallinity analysis showed that crystallization improved in all nanocomposites irrespective of surface modification; the thermogravimetric analysis showed that the imidazolium modified polymer composites are more thermally stable than conventional ammonium modified composites. The Transmission Electron Microscopy (TEM) analyses indicated that the PP-IMMT composites displayed exfoliated morphologies compared with the intercalated structure in PP-AMMT, and the rheological analysis at 180 ∘ C showed an enhancement in the viscoelastic properties as the clay concentration increases. The melt viscosity, crossover modulus, and relaxation times were comparable for both the surface modified composites with two different cations. The imidazolium based surfactant was found to be an effective organic modification for MMT to prepare thermally stable PP/MMT nanocomposites.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.