Z-PRIME Plus primer application after air-abrasion presented the best results for improving the bond strength between Y-TZP ceramic and self-adhesive resin cement.
The purpose of this study was to evaluate the effect of various surface treatments on the shear bond strength of Y-TZP (Yttria-Tetragonal Zirconia Polycrystal) ceramics with zirconia primer and two different resin cements both containing 10-methacryloyloxydecyl dihydrogen phosphate (MDP). Zirconia blocks (LAVA, 3M ESPE, St. Paul, MN) were polished and assigned to five groups according to the surface treatment: (1) no further treatment (control); (2) airborne abrasion with Al2 O3 particles; (3) Z-PRIME Plus (Bisco, Schaumburg, IL) applied on polished zirconia; (4) Z-PRIME Plus applied on zirconia after airborne abrasion; and (5) tribochemical silica-coating performed with the CoJet system (3M ESPE) followed by application of ESPE®-Sil (3M ESPE). Each group was further divided into one of two resin cements: Panavia F2.0 (Kuraray, Kurashiki, Okayama, Japan) and Clearfil SA Luting (Kuraray). Resin cement placed inside a gel-cap was polymerized on the zirconia surface. Shear bond strength was tested with a universal testing machine at 0.5 mm/min. One-way analysis of variance and paired t-test were done. (p < 0.05), and scanning electron microscope (SEM) images were taken. Zirconia primer applied after airborne abrasion significantly increased the shear bond strength resulting in the highest value for both resin cements. Control groups for both cements showed the weakest value for shear bond strength. No significant differences were found between the shear bond strengths of the individual resin cements applied to zirconia surfaces treated the same way. In conclusion, the combined surface treatment of airborne abrasion followed by a zirconia primer is recommended for zirconia bonding with Panavia F2.0 and Clearfil SA Luting cements.
The purpose of the study was to investigate the influence of 3D printing parameters on fit and internal gap of 3D printed resin dental prosthesis. The dental model was simulated and fabricated for three-unit prostheses with two implants. One hundred prostheses were 3D printed with two-layer thicknesses for five build orientations using a resin (NextDent C&B; 3D systems, Soesterberg, The Netherlands) and ten prostheses were manufactured with a milling resin as control. The prostheses were seated and scanned with micro-CT (computerized tomography). Internal gap volume (IGV) was calculated from 3D reconstructed micro-CT data. IGV, marginal fit, and lengths of internal gaps were measured, and the values were analyzed statistically. For the 3D printed prostheses, IGV was smaller at 45°, 60°, and 90° compared to other build orientations. The marginal fit evaluated by absolute marginal discrepancy was smaller than other build orientations at 45° and 60°. IGV was smaller at 50 µm layer thickness than at 100 µm layer thickness, but the marginal fit was smaller at 100 µm layer thickness than at 50 µm layer thickness. The 3D printed prosthesis had smaller internal gap than the milled prosthesis. The marginal fit of the 3D printed resin prosthesis was clinically acceptable, and build orientation of 45° and 60° would be recommended when considering fit and internal gap.
Purpose. This study was conducted to evaluate the effects of different phosphate monomer-containing primers on the shear bond strength between yttria-tetragonal zirconia polycrystal (Y-TZP) ceramics and MDP-containing self-adhesive resin cement. Materials and Methods. Y-TZP ceramic surfaces were ground flat with #600-grit SiC paper and divided into six groups (n = 10). They were treated as follows: untreated (control), Metal/Zirconia Primer, Z-PRIME Plus, air abrasion, Metal/Zirconia Primer with air abrasion, and Z-PRIME Plus with air abrasion. MDP-containing self-adhesive resin cement was applied to the surface-treated Y-TZP specimens. After thermocycling, a shear bond strength test was performed. The surfaces of the Y-TZP specimens were analyzed under a scanning electron microscope. The bond strength values were statistically analyzed using one-way analysis of variance and the Student–Newman–Keuls multiple comparison test (P < 0.05). Results. The Z-PRIME Plus treatment combined with air abrasion produced the highest bond strength, followed by Z-PRIME Plus application, Metal/Zirconia Primer combined with air abrasion, air abrasion alone, and, lastly, Metal/Zirconia Primer application. The control group yielded the lowest results (P < 0.05). Conclusion. The application of MDP-containing primer resulted in increased bond strength between Y-TZP ceramics and MDP-containing self-adhesive resin cements.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.