No abstract

The urbanization process contributes to the growth of solid waste generation and causes an increase in environmental impacts and failures in the management of solid waste. The number of dumps is a concern due to the limited implementation and safe disposal of this waste. The interest in sustainable techniques has been growing in relation to waste management, which is largely absorbed by the civil construction sector. This work aimed to review plastic waste, especially polyethylene terephthalate (PET), that can be incorporated with construction materials, such as concrete, mortars, asphalt mixtures, and paving. The use of life-cycle assessment (LCA) is related, as a tool that allows the sustainability of products and processes to be enhanced in the long term. After analyzing the recent literature, it was identified that studies related to plastic wastes in construction materials concentrate sustainability around the alternative destination of waste. Since the plastic waste from different production chains are obtained, it was possible to affirm the need for a broader assessment, such as the LCA, providing greater quantification of data making the alternative processes and products more sustainable. The study contributes to enhance sustainability in alternative building materials through LCA.

No abstract

Brazil is one of the largest producers of pineapple in the world, which, in addition to bringing substantial benefits, contributes to increasing waste generation in the stages of processing, aiming at its consumption. The Brazilian environmental legislation has been increasingly more restrictive with respect to the disposal of solid waste, whether domestic, industrial or agro-industrial, which has stimulated studies related to the use of these materials in several matrices. This study aimed to evaluate the potentiality of using the natural fiber of pineapple (Ananas comosus), extracted from its leaves, as reinforcing material in cementitious composites. For this purpose, natural fiber extracted from the pineapple crown was incorporated in different percentages in relation to the cement mass: 0, 2.5, 5, 7.5 and 10%, and the fibers obtained were submerged in aqueous NaOH solution with 5% concentration in volume, for 1 h at room temperature. The following variables were evaluated: consistency, water retention, incorporated air, mass density in hardened state, mechanical strength, water absorption by immersion and capillarity, besides verifying the influence of the mode of fiber incorporation. It was observed that the treatment with NaOH solution and the percentage of natural pineapple fiber incorporated in up to 5% in relation to the cement mass form mortars with technological feasibility.

No abstract

No abstract

Lignocellulosic material residues in cement composites are a favourable option for new fibre cement formulations in building materials, because they combine good mechanical properties with low density. This study aimed to evaluate the chemical, physical, anatomical, and mechanical properties of five cement panels reinforced with the following lignocellulosic materials: eucalyptus, sugarcane bagasse, coconut shell, coffee husk, and banana pseudostem. Lignocellulosic cement panels were produced with each lignocellulosic material residue, and three replicates of each type of lignocellulosic material were examined (15 panels in total). The lignin, extractives, ash, and holocellulose were examined. After 28 days of composite curing, the following physical properties of the panels were evaluated: density, porosity, water absorption after immersion for 2 and 24 h, and thickness swelling after immersion for 2 and 24 h. Mechanical tests (compression strength, internal bonding, modulus of rupture, and modulus of elasticity) were performed before and after the accelerated ageing test with a universal testing machine. Scanning electron microscopy and supervised image classification were performed to investigate the morphologies of the different materials and the filler/matrix interfaces. Eucalyptus and sugarcane panels had the best results in terms of the evaluated properties and thus, could potentially be used as non-structural walls. However, banana pseudostem, coconut shell, and coffee husk panels had the worst results and therefore, under these conditions, should not be used in building.

The ever-growing consumption and improper disposal of non-biodegradable plastic wastes is bringing worrisome perspectives on the lack of suitable environmentally correct solutions. Consequently, an increasing interest in the circular economy and sustainable techniques is being raised regarding the management of these wastes. The present work proposes an eco-friendly solution for the huge amount of discarded polyethylene terephthalate (PET) wastes by addition into soil-cement bricks. Room temperature molded 300 × 150 × 70 mm bricks were fabricated with mixtures of clay soil and ordinary Portland cement added with up to 30 wt.% of PET waste particles. Granulometric analysis of soil indicated it as sandy and adequate for brick fabrication. As for the PET particles, they can be considered non-plastic and sandy. The Atterberg consistency limits indicated that addition of 20 wt.% PET waste gives the highest plasticity limit of 17.3%; moreover, with PET waste addition there was an increase in the optimum moisture content for the compaction and decrease in specific weight. Standard tests showed an increase in compressive strength from 0.83 MPa for the plain soil-cement to 1.80 MPa for the 20 wt.% PET-added bricks. As for water absorption, all bricks displayed values between 15% and 16% that attended the standards and might be considered an alternative for non-structural applications, such as wall closures in building construction.