The wake-up behavior of ferroelectric thin film capacitors based on doped hafnium oxide dielectrics in TiN-based metal-insulator-metal structures is reported. After field cycling a remanent polarization up to 40 C/cm 2 and a high coercive field of about 1MV/cm was observed. Doping of HfO2 by different dopants with a crystal radius ranging from 54pm (Si) to 132pm (Sr) was evaluated. In all cases, an improved polarization-voltage hysteresis after wake-up cycling is visible. For smaller dopant atoms like Si and Al stronger pinching of the polarization hysteresis appeared with increasing dopant concentration and proved to be stable during cycling. ©2014 The Japan Society of Applied Physics

With the ability to engineer ferroelectricity in HfO2 thin films, manufacturable and highly scaled MFM capacitors and MFIS-FETs can be implemented into a CMOS-environment. NVM properties of the resulting devices are discussed and contrasted to existing perovskite based FRAM

No abstract

Thin film capacitors were fabricated by sputtering TiN-Y doped HfO2-TiN stacks on silicon substrates. Yttrium was incorporated into the HfO2 layers by simultaneously sputtering from Y2O3 and HfO2 sources. Electric polarization and relative permittivity measurements yield distinct ferroelectric properties as a result of low yttrium dopant concentrations in the range of 0.9-1.9 mol. %. Grazing incidence x-ray diffraction measurements show the formation of an orthorhombic phase in this range. Compared to atomic layer deposition films, the highest remanent polarization and the highest relative permittivity were obtained at significantly lower doping concentrations in these sputtered films

Static domain structures and polarization dynamics of silicon doped HfO2 are explored. The evolution of ferroelectricity as a function of Si-doping level driving the transition from paraelectricity via ferroelectricity to antiferroelectricity is investigated. Ferroelectric and antiferroelectric properties can be observed locally on the pristine, poled and electroded surfaces, providing conclusive evidence to intrinsic ferroic behavior.

No abstract

No abstract

No abstract