No abstract

Tissue engineering is widely recognized as a promising approach for bone repair and reconstruction. Several attempts have been made to achieve materials that must be compatible, osteoconductive, and osteointegrative and have mechanical strength to provide a structural support. Composite scaffolds consisting in biodegradable natural polymers are very promising constructs. Hydroxyapatite (HAp) can support alginate as inorganic reinforcement and osteoconductive component of alginate/HAp composite scaffolds. Therefore, HAp-strengthened polymer biocomposites offer a solid system to engineer synthetic bone substitutes. In the present work, HAp was incorporated into an alginate solution and internal gelling was induced by addition of slowly acid-hydrolyzing D-gluconic acid delta-lactone for the direct release of calcium ions from HAp. It has been previously demonstrated that alginate-based composites efficiently support adhesion of cancer bone cell lines. Human dental pulp stem cells (DPSCs) identified in human dental pulp are clonogenic cells capable of differentiating in multiple lineage. Thus, this study is aimed at verifying the mineralization and differentiation potential of human DPSCs seeded onto scaffolds based on alginate and nano-hydroxyapatite. For this purpose, gene expression profile of early and late mineralization-related markers, extracellular matrix components, viability parameters, and oxidative stress occurrence were evaluated and analyzed. In summary, our data show that DPSCs express osteogenic differentiation-related markers and promote calcium deposition and biomineralization when growing onto Alg/HAp scaffolds. These findings confirm the use of Alg/HAp scaffolds as feasible composite materials in tissue engineering, being capable of promoting a specific and successful tissue regeneration as well as mineralized matrix deposition and sustaining natural bone regeneration.

No abstract

No abstract

Collagen membranes are used in oral surgery for bone defects treatment acting as a barrier that does not allow the invasion of soft tissue into the growing bone. To improve biocompatibility collagen membranes were coated with graphene oxide (GO), a graphene derivative. The aim of this study was to investigate the biocompatibility of GO coated collagen membranes on human dental pulp stem cells (DPSCs) focusing on biomaterial cytotoxicity, ability to promote DPSCs differentiation process and to control inflammation event induction. DPSCs were cultured on uncoated membranes and on both 2 and 10 μg mL GO coated membranes up to 28 days. Alamar blue and LDH cytotocicity assay, PGE2 ELISA assay, real time RT-PCR for RUNX2, BMP2, SP7, TNFα and COX2 genes expression were performed. Proliferation is higher on GO coated membranes at days 14 and 28. LDH assay evidences no cytotoxicity. BMP2 and RUNX2 expression is higher on coated membranes, BMP2 at early and RUNX2 and SP7 at late experimental times. PGE2 levels are lower on GO coated membranes at days 14 and 28, both TNFα and COX2 expression is significantly decreased when GO is applied. GO coated membranes are not toxic for DPSCs, induce a faster DPSCs differentiation into odontoblasts/osteoblasts and may represent good alternative to conventional membranes thus ensuring more efficient bone formation and improving the clinical performance. © 2017 Wiley Periodicals, Inc. J Biomed Mater Res Part A: 105A: 2312-2320, 2017.

No abstract

No abstract

No abstract