No abstract

In this work, a maleinized soybean oil (SOMA) was melt reacted with polyamide 6 and the thermal, rheological, and morphological properties were evaluated. It was observed that the maleinized soybean oil reacted with polyamide chains, increasing the molecular weight of the polymer. Addition of SOMA also promoted an increase in the amount of α crystalline phase as well as in the crystallinity index. The average amorphous layer thickness (La) was enhanced with the addition of 1 wt % of SOMA, while the average crystalline layer thickness (Lc) were significantly enlarged with the increase in SOMA content, indicating that SOMA structures were located at the interfacial region between amorphous and crystalline. The addition of 5 wt % of SOMA plasticized the PA6, reducing its glass transition temperature. However, the sample containing 5 wt % of SOMA showed an accentuated pseudoplastic behavior as compared to other samples. Addition of SOMA also reduced the tensile strength and increased the elongation at break. © 2015 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2016, 133, 43050.

No abstract

No abstract

No abstract

Poliedros oligoméricos silsesquioxanos (POSS) são estruturas híbridas tipo (RSiO1,5)n com n grupos orgânicos R. Estas moléculas podem ser facilmente funcionalizadas, simplesmente alterando a constituição química dos grupos orgânicos. Nesse trabalho, a modificação química de POSS-NH2 foi feita por meio de reações de amidação comácido butírico em elevada temperatura, 160 o C. A formação do novo grupo amidaé evidenciada pelo do surgimento da banda de deformação angular do NH em 1540 cm −1 nos espectros de FTIR. Aproximadamente 40% dos grupos aminos reagiram, conforme resultados de titulação. A formação dos grupos amidas resultou no deslocamento da temperatura de transição vítrea (Tg) de-36,9 o C para-25,6 o C para o POSS-modificado. Ambas as amostras, de POSS-NH2 e POSS-modificado, exibem padrão de degradação térmica semelhante. A análise da função de distribuição de pares (PDF) determinou que as nanopartículas híbridas são separadas por uma distância periódica de aproximadamente 1,32 nm. O POSS-NH2 e o POSS-modificado apresentam comportamento newtoniano, na faixa que vai de 10 −1 s −1 até 1000 s −1. A viscosidade diminuiu com aumento da temperatura, um comportamento típico de lubrificantes líquidos.

Recebido em 21/11/07; aceito em 24/7/08; publicado na web em 15/12/08 STUDY OF MCM-71 ZEOLITE SYNTHESIS. A new kind of material, denominated MCM-71, was synthesized and characterized by several complementary techniques: X Ray Diffractometry, textural analysis by nitrogen adsorption, Scanning electronic microscopy and infrared spectroscopy. MCM-71 zeolite was successfully synthesized by hydrothermal synthesis in the presence of triethanolamine. Mordenite phase as impurity was not detected, otherwise quartz was observed. The MCM-71 sample obtained presented a BET surface area of 20 m 2 /g in the as synthesized form and of 85 m 2 /g in protonic form. By SEM was observed crystals with rectangular shape with average size of 2 x 0,2 x 0,05 µm and this crystals were agglomerated in spherical particles with average diameter between 14 and 24 µm.Keywords: MCM-71; zeolites; synthesis. intRoduÇÃoZeólitas são compostos microporosos que apresentam um papel importante em vários áreas tecnológicas, principalmente como catalisadores.1,2 As razões de seu êxito em catálise são sua alta área superficial, capacidade de adsorção, seus centros ácidos, tamanhos de seus canais e cavidades e sua seletividade de forma. Estas características fazem com que as zeólitas sejam materiais interessantes para serem utilizados também como trocadores iônicos, peneiras moleculares e adsorventes. Neste sentido é interessante sempre buscar novos materiais zeolíticos ainda pouco estudados.A síntese da zeólita MCM-71 foi descrita recentemente. 3,4 Esse novo material possui um sistema de canais tridimensionais retos, de abertura elíptica, formados por 10 MR (0,65 x 0,43 nm) que são intersectados por outro sistema de canais senozoidais definidos por abertura de 8 MR (0,47 x 0,36 nm), Figura 1.Este material foi sintetizado com uma relação Si/Al ∼8, que faz que seja um catalisador interessante para reações ácido-base. Zeóli-tas de poros médios têm sido empregadas em reações que requerem seletividade de forma, tais como adição de amina no metanol para produzir monometilamina pela inibição da formação de di-e trimetilamine; em reações de isomerização de n-alcanos de frações leves de nafta para aumento da octanagem e, em reações de reforma catalítica do diesel pela remoção seletiva de parafinas de cadeias lineares para aumentar o índice de viscosidade do produto. A forma protonada do material, H +

No abstract