CuIn 2n+1 S 3n+2 crystals were synthesized by horizontal Bridgman method using high purity copper, indium, sulfur elements. The phases and crystallographic structure of the CuIn 2n+1 S 3n+2 crystals were analyzed by X-ray diffraction (XRD) and the composition of the material powders was determined using the energy dispersive X-ray analysis (EDX). Measurement data revealed that CuIn 2n+1 S 3n+2 materials have not the same structure. In fact, CuInS 2 and CuIn 3 S 5 crystallize in the chalcopyrite structure whereas CuIn 5 S 8 , CuIn 7 S 11 and CuIn 11 S 17 crystallize in the cubic spinel structure.
RF sputtered undoped and Cu doped ZnO (CZO) thin films were deposited on unheated glass substrates using a mixed Cu2O and ZnO powders target at different Cu concentrations of 0, 1, 2, 3 and 4 wt.%. The effects of copper concentration on the structural, electrical, optical and photocatalytic properties of CZO films have been studied.From XRD and Raman spectroscopy studies, it was found that the deposited films were polycrystalline with a predominant hexagonal wurtzite structure along the c-axis perpendicular to the substrate surface. The presence of multiple interference fringes in the transmittance and reflectance spectra shows the good homogeneity of the films.All the films are highly transparent with transparency reaching 80% indicating the possibility to use these films as an optical window. The absorption tail gradually shifted towards a higher wavelength side, which resulted in the decrease of bandgap energy from 3.35 to 3.26 eV. All the sputtered films are highly conductive with a conductivity reaching 10 4 S.cm -1 .The effect of Cu-doping on the photocatalytic activity of ZnO thin films for the degradation of methylene blue (MB) dye was studied under sunlight irradiation and the results showed that the Cudoping provokes appreciable degradation of MB and reached a maximum for the 1 wt.% Cu doped ZnO film.
RF sputtered undoped and Cu doped ZnO (CZO) thin films were deposited on unheated glass substrates using a mixed Cu2O and ZnO powders target at different Cu concentrations of 0, 1, 2, 3 and 4 wt.%. The effects of copper concentration on the structural, electrical, optical and photocatalytic properties of CZO films have been studied. From XRD and Raman spectroscopy studies, it was found that the deposited films were polycrystalline with a predominant hexagonal wurtzite structure along the c-axis perpendicular to the substrate surface. The presence of multiple interference fringes in the transmittance and reflectance spectra shows the good homogeneity of the films. All the films are highly transparent with transparency reaching 80% indicating the possibility to use these films as an optical window. The absorption tail gradually shifted towards a higher wavelength side, which resulted in the decrease of bandgap energy from 3.35 to 3.26 eV. All the sputtered films are highly conductive with a conductivity reaching 104 S.cm− 1.The effect of Cu-doping on the photocatalytic activity of ZnO thin films for the degradation of methylene blue (MB) dye was studied under sunlight irradiation and the results showed that the Cudoping provokes appreciable degradation of MB and reached a maximum for the 1 wt.% Cu doped ZnO film.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.