Multi-walled carbon nanotubes (MWCNT) promoted by oxides, that are far from trivial to characterize, have emerged as promising candidates in several fields such as biosensors and catalysis. In this study the coverage of ZrO 2 nanoparticles supported on MWCNT, by carbonaceous deposits or tungstates was investigated by NO x temperatureprogrammed desorption (NO x -TPD). ZrO 2 coverage by carbonaceous deposits was found to be about 30 %, whereas that by tungstates varied from 40 to 77 % depending on the W loading of the sample. The size of the ZrO 2 particles estimated by NO x -TPD (~2.3 nm) was found to be in excellent agreement with that determined by TEM. Remarkably, it was found that W interacted preferentially with the ZrO 2 nanoparticles for a W surface density of 1.9 W/nm 2 ZrO2 (half monolayer coverage of the ZrO 2 nanoparticles by tungstates). Monolayer coverage of ZrO 2 by tungstates was nearly complete when introducing a W loading twice as high as that theoretically needed. These insights into the surface coverage of ZrO 2 by carbon or tungstates could not be obtained by any means other than NO x -TPD, which makes it a unique method to provide advanced characterization of the surface of oxides supported on MWCNT, in particular, and carbon supports, to a broader general interest.