In this study, the influence of micro-and nano-filler content on the mechanical properties of epoxy composites was studied. The matrix material is epoxy; the micro-fillers are Al 2 O 3 , TiO 2 and fly ash added in 10 wt% to 30 wt% by weight ratio; the nano-fillers are Al 2 O 3 , TiO 2 and clay added in 2.5 wt% to 10 wt% by weight ratio. Test samples were prepared using an open mould type die. Tensile, three-point bending and hardness tests were carried out. The tensile strength, elastic modulus, elongation at break, flexural strength, flexural modulus, and the hardness of the composite materials were obtained and evaluated. The results show that the tensile strength, flexural strength and elongation at the break values of composites decreased while the tensile modulus and flexural modulus increased with the increasing micro-and nano-filler content ratio.
Sliding wear performance of 20% mica-filled polyamide 6 (PA6 + 20% mica) and 20% short glass fibrereinforced polysulphone (PSU + 20 GFR) polymer composites used in electrical applications were investigated using a pin-on-disc wear test apparatus. Two different disc materials were used in this study. These are AISI 316 L stainless steel and 30% glass fibre-reinforced polyphenylenesulphide (PPS + 30%GFR) polymer composite. Wear test was carried out at 10, 20 and 30 N applied load values and 0•5 m/s sliding speed and at ambient temperature and humidity. Different combinations of rubbing surfaces were examined and friction coefficient and specific wear rate values were obtained and compared. For two material combinations used in this investigation, the coefficient of friction shows insignificant sensitivity to applied load values and large sensitivity to material combinations. For specific wear rate, PA6 + 20% mica composite has shown insensitivity to change in load, speed and materials combination while PSU + 20% glass fibre composite has shown high sensitivity to the change in load and material combinations. The friction coefficient of PA6 + 20% mica and PSU + 20 glass fibre rubbing against the AISI 4140 steel disc is between 0•35 and 0•40. In rubbing against PPS + 30% glass fibre their values were between 0•25 and 0•30. Specific wear rate for PA6 + 20% mica and PSU + 20% glass fibre composites are in the order of 10 −13 to 10 −14 m 2 /N. Finally, the wear mechanisms are a combination of adhesive and abrasive wear processes. In terms of application, especially in electrical systems, a substantial contribution was provided to extend switch life. Thus, besides robustness, this also ensured safety for the system and the users against undesirable situations.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.