No abstract

We fabricated crack self-healing capsules using cement powder for mixing into cement composites and evaluated the properties of the capsule manufacturing process in this study. The manufacture of the self-healing capsules is divided into core production processing of granulating cement in powder form and a coating process for creating a wall on the surfaces of the granulated cement particles. The produced capsules contain unhardened cement and can be mixed directly with the cement composite materials because they are protected from moisture by the wall material. Therefore, the untreated cement is present in the form of a capsule within the cement composite, and hydration can be induced by moisture penetrating the crack surface in the event of cracking. In the process of granulating the cement, it is important to obtain a suitable consistency through the kneading agent and to maintain the moisture barrier performance of the wall material. We can utilize the results of this study as a basis for advanced self-healing capsule technology for cement composites.

An experimental study was carried out to evaluate fresh properties of a moderately high-strength (high-flowing) selfcompacting concrete (SCC) and to investigate shear behavior and performance of deep beams made with SCC. Fresh and hardened properties of normal concrete (NC) and SCC were evaluated. The workability and compacting ability were observed based on casting time and number of surface cavities, respectively. Four-point loading tests on four deep beams (two made with SCC and two with NC) were then conducted to investigate their shear behavior and performance. Shear behavior and performance of beams having two different web reinforcements in shear were systematically investigated in terms of crack pattern, failure mode, and load-deflection response. It was found from the tests that the SCC specimen having a normal shear reinforcement condition exhibited a slightly higher load carrying capacity than the corresponding NC specimen, while the SCC specimen having congested shear reinforcement condition showed a similar load carrying capacity to the corresponding NC specimen. In addition, a comparative study between the present experimental results and theoretical results in accordance with ACI 318 (Building Code Requirements for Reinforced Concrete (ACI 318-89) and Commentary-ACI 318R-89, 1999), Hsu-Mau's explicit method (Hsu, Cem Concr Compos 20:419-435, 1998; Mau and Hsu, Struct J Am Concr Inst 86:516-523, 1989) and strut-and-tie model suggested by Uribe and Alcocer (2002) based on ACI 318 Appendix A (2008) was carried out to assess the applicability of the aforementioned methods to predict the shear strength of SCC specimens.

This study was evaluated influence of fluidity properties according to basalt fiber and high volume fly ash in the mortar level, as part of a basic study for development of fiber reinforced concrete using basalt fiber and high volume fly ash. In the first step, it was evaluated that fluidity properties of mortar according to replacement ratio 6 level of fly ash(10, 20, 30, 40, 50 and 60mass%) and fluidity properties of mortar according to content 5 levels of SP(1.3, 1.5, 1.7, 1.9 and 2.1%) and content 5 levels of VA(0.2, 0.4, 0.6, 0.8 and 1.0%) for dispersion of the basalt fiber, in the second step, it was evaluated that fluidity properties of mortar using High-volume fly ash (50mass%) on 3 levels of basalt fiber length (6, 20 and 30mm). Results of assessment, if after a fiber mixed, it showed that viscosity agent is more effective to improve the fluidity and fiber dispersion than superplasticizer, high volume fly ash (50%) applying the mixing, due to three properties of fly ash, showed that the improved fiber dispersibility and flow improvement.

Self-healing cement composites are generally produced by using materials such as inorganic powders, bacteria pellets, and microcapsules. Among them, inorganic powder-type healing materials tend to decrease in healing performance over time because they react relatively quickly. Accordingly, this study encapsulated self-healing inorganic reactive powders in solid capsules (SC) in order to delay their reaction. The capsule surface was coated with a membrane to prevent moisture from permeating it. SC were utilized to provide the self-healing effect to the repair mortar. SC were mixed at three rates (0%, 5%, and 10%) by the binder mass of the repair mortar. The fundamental properties, including rheology, table flow, strength, and length change, and the self-healing performance of the self-healing repair mortar mixes were investigated. It was found that the rheological and mechanical properties of the repair mortar decreased slightly as the amount of SC increased. On the other hand, for a crack width of 0.25 mm and crack inducing age of 28 days, the healing performance of repair mortar specimens containing SC was at least 20 pt% better than that of plain repair mortar after a healing period of 28 days.