No abstract

To improve water-resistant ability and mechanical properties of silk fibroin (SF)/hydroxybutyl chitosan (HBC) nanofibrous scaffolds for tissue-engineering applications, genipin, glutaraldehyde (GTA), and ethanol were used to crosslink electrospun nanofibers, respectively. The mechanical properties of nanofibrous scaffolds were obviously improved after 24 h of crosslinking with genipin and were superior to those crosslinked with GTA and ethanol for 24 h. SEM indicated that crosslinked nanofibers with genipin and GTA vapor had good water-resistant ability. Characterization of the microstructure (porosity and pore structure) demonstrated crosslinked nanofibrous scaffolds with genipin and GTA vapor had lager porosities and mean diameters than those with ethanol. Characterization of FTIR-ATR and (13)C NMR clarified both genipin and GTA acted as crosslinking agents for SF and HBC. Furthermore, genipin could induce SF conformation from random coil or α-helix to β-sheet. Although GTA could also successfully crosslink SF/HBC nanofibrous scaffolds, in long run, genipin maybe a better method due to lower cytotoxicity than GTA. Cell viability studies and wound-healing test in rats clarified that the genipin-crosslinked SF/HBC nanofibrous scaffolds had a good biocompatibility both in vitro and in vivo. These results suggested that genipin-crosslinked SF/HBC nanofibrous scaffolds might be potential candidates for wound dressing and tissue-engineering scaffolds.

The aim of this study is to investigate cross-linked gelatin-chitosan nanofibers produced by means of electrospinning. Gelatin and chitosan nanofibers were electrospun and then cross-linked by glutaraldehyde (GTA) vapor at room temperature. Scanning electron microscopy (SEM) images showed that the cross-linked mats could keep their nanofibrous structure after being soaked in deionized water at 37° C. The cross-linking mechanism was discussed based on FT-IR results. The two main mechanisms of cross-linking for chitosan and gelatin-chitosan complex are Schiff base reaction and acetalization reaction. For gelatin, the mechanism of cross-linking was Schiff base reaction. The mechanical properties of nanofibrous mats were improved after cross-linking. The biocompatibility of electrospun nanofibrous mats after cross-linking was investigated by the viability of porcine iliac endothelial cells (PIECs). The morphologies of PIECs on the cross-linked nanofibrous mats were observed by SEM. In addition, proliferation of PIECs was tested with the method of methylthiazol tetrazolium (MTT) assay. The results indicate that gelatin-chitosan nanofibrous mats could be a promising candidate for tissue-engineering scaffolds.

Design and fabrication of nanofibrous scaffolds should mimic the native extracellular matrix. This study is aimed at investigating electrospinning of polycaprolactone (PCL) blended with chitosan-gelatin complex. The morphologies were observed from scanning electron microscope. As-spun blended mats had thinner fibers than pure PCL. X-ray diffraction was used to analyze the degree of crystallinity. The intensity at two peaks at 2θof 21° and 23.5° gradually decreased with the percentage of chitosan-gelatin complex increasing. Moreover, incorporation of the complex could obviously improve the hydrophilicity of as-spun blended mats. Mechanical properties of as-spun nanofibrous mats were also tested. The elongation at break of fibrous mats increased with the PCL content increasing and the ultimate tensile strength varied with different weight ratios. The as-spun mats had higher tensile strength when the weight ratio of PCL to CS-Gel was 75/25 compared to pure PCL. Both as-spun PCL scaffolds and PCL/CS-Gel scaffolds supported the proliferation of porcine iliac endothelial cells, and PCL/CS-Gel had better cell viability than pure PCL. Therefore, electrospun PCL/Chitosan-gelatin nanofibrous mats with weight ratio of 75/25 have better hydrophilicity mechanical properties, and cell proliferation and thus would be a promising candidate for tissue engineering scaffolds.

An excellent turn-on and colorimetric fluorescent chemosensor DCF-MPYM-thiol for sensing Cys based on metal-free organic fluorophores has been synthesized.