In this article, the laser-based powder bed fusion (L-PBF) processing behavior of pure copper powder is evaluated by employing a conventional infrared fiber laser with a wavelength of 1080 nm, a small focal spot diameter of 37.5 µm, and power levels up to 500 W. It is shown that bulk solid copper parts with near full density (ρ Archimedes = 99.3 ± 0.2%, ρ Optical = 99.8 ± 0.1%) can be produced using a laser power of 500 W for the chosen combination of powder particle size, L-PBF settings, and pure copper baseplate. Moreover, at 500 W, parts with a relative density exceeding 99% are manufactured within a volumetric energy density window of 230 -310 J/mm 3 , while laser power levels below 500 W did not produce parts with a relative density above 99%. An analytical model is used to elucidate the L-PBF processing behavior, wherein both conduction and keyhole regimes corresponding to the employed L-PBF settings are identified. The analytical model-based results predict that the bulk solid copper parts with near full density are produced in a keyhole regime prior to the onset of keyholeinduced porosity, which is in accordance with the porosity types observed in the parts. The L-PBF fabricated copper parts exhibit an electrical conductivity of 94 ± 1% compared to the international annealed copper standard (IACS) and demonstrate a tensile strength of 211 ± 4 MPa, a yield strength of 122 ± 1 MPa, and an elongation at break of 43 ± 3% in the as-built condition.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.