In silicon heterojunction (SHJ) solar cells, a wide bandgap material with a high work function is widely used as the hole extraction pathway to attain high efficiency. We introduced a molybdenum oxide (MoOx) film as an effective hole-transfer layer in carrier selective contact (CSC) solar cells by virtue of its wide bandgap along with high work function. The passivation characteristics, and optical and electrical properties of MoOx films were investigated by differing thickness and work function. The combination of 6 nm hydrogenated intrinsic amorphous silicon (a-Si:H(i)) and 7 nm thermally evaporated MoOx passivation layers provides excellent passivation properties, reduces carrier recombination, and improves the cell performance. The synthesized CSC solar cells showed promising results, with an open-circuit voltage (Voc) of 708 mV, short-circuit current (Jsc) = 37.38 mA/cm2, fill factor (FF) = 74.59%, and efficiency (η) = 19.75%. To justify the obtained result, an AFORS HET simulation was conducted based on the experimental results. The high work function and wide bandgap MoOx/c-Si(n) interface developed a considerable built-in potential and suppressed the electron–hole pair recombination mechanism. The CSC solar cell's simulated performance was enhanced from 1.62 to 23.32% by varying MoOx work function (ΦMoOx) from 4.5 to 5.7 eV.
Corrosion accounts for 52% of the recorded breakdown of insulators utilized in transmission lines, which may interfere with the reliability of power utilities. The CeO2 conversion coating, CeO2-ethylene propylene diene monomer, EPDM composite coating, and Perfluoropolyether PFPE lubricating oil-infused hydrophobized CeO2 composite surfaces were developed on the insulator surface to address these challenges. The properties of these three kinds of structures are compared based on the persistence of coating over insulators installed in a highly contaminated environment. PFPE lubricating oil-infused hydrophobized CeO2 composite surfaces show excellent performance over other approaches. A lubricating oil-infused hydrophobized CeO2 composite of thickness 35.4 µm exhibits contact angles 60°, 85°, and 160°, and contact angle hysteresis of 12°, 10°, and 4°, respectively, after accelerated thermal aging. The proposed approach presents self-healing and corrosion resistance (corrosion rate 0.3 × 10−3 mm/Y, Icorr 1.2 × 10−7), post-accelerated thermal aging. The research outcome is expected to pave the way for incredibly robust insulator coatings.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.