Most implantable medical devices are expected to function in the body over an extended period of time. Therefore, immersion tests under simulated conditions can be useful for assessing the amount of metal ions released in situ. In this investigation, dissolved ions from as-received binary and ternary Nitinol alloys in cell culture media were periodically measured under static and dynamic conditions. Endothelial cells were grown in aliquots of culture media obtained and the effect of dissolved ions on cell proliferation and viability of endothelial cells (HUVEC) was studied by cytotoxicity assays. The concentration of metal ions in the media was measured by inductively coupled plasma mass spectrometry.

No abstract

Nitinol (an acronym for the Nickel-Titanium Naval Ordnance Laboratory) has been extensively explored as an implant material for the medical industry. The potential problem with Nitinol implant devices is the release of Ni in the human body, which has stimulated a great deal of research on surface modifications and the application of coatings. This paper presents a comprehensive review of various treatments to modify the surface of Nitinol in an effort to inhibit Ni release and to render improved biocompatibility. We discuss the important in-service properties of Nitinol, such as biocompatibility, corrosion resistance, stability, uniformity, and the nature of passivating oxides produced by passivation, electropolishing, magnetoelectropolishing, ion beam implantation, sterilization, and artificial coatings.

ObjectivesTo determine the incidence of crack formation and propagation in apical root dentin after retreatment procedures performed using ProTaper Universal Retreatment (PTR), Mtwo-R, ProTaper Next (PTN), and Twisted File Adaptive (TFA) systems.Materials and MethodsThe study consisted of 120 extracted mandibular premolars. One millimeter from the apex of each tooth was ground perpendicular to the long axis of the tooth, and the apical surface was polished. Twenty teeth served as the negative control group. One hundred teeth were prepared, obturated, and then divided into 5 retreatment groups. The retreatment procedures were performed using the following files: PTR, Mtwo-R, PTN, TFA, and hand files. After filling material removal, apical enlargement was done using apical size 0.50 mm ProTaper Universal (PTU), Mtwo, PTN, TFA, and hand files. Digital images of the apical root surfaces were recorded before preparation, after preparation, after obturation, after filling removal, and after apical enlargement using a stereomicroscope. The images were then inspected for the presence of new apical cracks and crack propagation. Data were analyzed with χ2 tests using SPSS 21.0 software.ResultsNew cracks and crack propagation occurred in all the experimental groups during the retreatment process. Nickel-titanium rotary file systems caused significantly more apical crack formation and propagation than the hand files. The PTU system caused significantly more apical cracks than the other groups after the apical enlargement stage.ConclusionsThis study showed that retreatment procedures and apical enlargement after the use of retreatment files can cause crack formation and propagation in apical dentin.

The effects of different obturation techniques on calcium silicate-based sealer penetration in the presence of apically separated rotary files were evaluated. Forty-eight extracted mandibular incisors were used. ProTaper F2 rotary files were separated at the apical thirds. Samples were divided into four groups (n = 12) according to obturation technique used: (a) cold lateral compaction (CLC); (b) single cone; (c) bulk-fill (BF) without a core material; and (d) thermoplastic injection (TI). Specimens were sectioned horizontally at 1 and 3 mm from the apex and studied using a confocal scanning laser microscope. The maximum tubule penetration depth and percentage of penetration were measured. Data were statistically analyzed using parametric and nonparametric tests with a significance level of 5%. Regarding penetration depth, a significant difference was found at 1 mm (p < .05), while no significant difference was found at 3 mm (p > .05). At the 3 mm level, all of the obturation techniques showed similar penetration depths. Regarding penetration percentage, the values of the CLC and TI groups were statistically less when compared with the BF group at 1 and 3 mm levels, respectively (p < .05). Under the limitations of this in vitro study, results suggest that the obturation technique may present a significant effect on sealer penetration. K E Y W O R D S confocal laser scanning microscope, obturation technique, sealer penetration, separated instruments

Objectives:The obturation quality of MTA, Biodentine, Total Fill BC root canal sealer (RCS), and warm gutta-percha (WGP) in teeth with simulated internal root resorption (IRR) was evaluated by using micro-computed tomography. Materials and Methods: Standardized IRR cavities were created using 40 extracted maxillary central incisor teeth and randomly assigned into 4 groups (n = 10). IRR cavities were filled with MTA, Biodentine, Total Fill BC RCS (bulk-fill form) and WGP + Total Fill BC RCS. Percentage of voids between resorptive cavity walls and obturation material (external void), and inside the filling materials (internal voids) were measured. Results: Total Fill BC sealer in the bulk-fill form presented significantly highest values of external and internal void percentages (p < 0.05). Biodentine showed a significantly lowest external void percentage (p < 0.05). WGP + Total Fill BC RCS presented significantly lower values of internal void percentages than all groups (p < 0.05), except Biodentine (p > 0.05). Conclusion:None of the filling materials were created void-free obturation in resorption cavities. Biodentine may favor its application in teeth with IRR over Angelus MTA and bulkfill form of Total Fill BC.