Mesa structures were etched in HgCdTe using different Br 2 /HBr/Ethylene glycol (EG) formulations. Etch rate and degree of anisotropy (A) were studied in detail for all of the combinations. Addition of EG to the conventional etchant gave A Ͼ 0.5, with controllable etch rates. Optimum etchant composition was determined to be 2% Br 2 in a 3:1 mixture of EG:HBr. This composition resulted in a good anisotropy factor of ϳ0.6 and a reasonably optimum etch rate of ϳ2.5 µm/min, with rms surface roughness of ϳ2 nm. Kinetics of the etching reaction have also been studied for the optimum etchant concentration and an etching mechanism has been proposed.
Bromine-and iodine-based solutions were compared for surface preparation of HgCdTe epilayers. The iodine (I)-potassium iodide (KI)-based non-aqueous solution for surface preparation of mercury cadmium telluride (HgCdTe) epilayers is less corrosive, less toxic and technologically more suitable compared to the widely used bromine-based etchants. It provides improved surface morphology and a lower amount of oxides. A comparative study of the oxide content and elemental tellurium residue on the polished surface was made by x-ray photoelectron spectrometry measurements. Least elemental Te content was observed on the HgCdTe surface polished with I-KI solution as compared to bromine-based etchants. It may result in reduced trap density at the surface of HgCdTe. The possibility of potassium diffusion due to I-KI polishing at the HgCdTe surface, as well as at the cadmium zinc telluride (CdZnTe)-HgCdTe interface, has been ruled out using secondary ion mass spectrometry. Performance of photodiodes fabricated on the polished epilayers (Hg 0.7 Cd 0.3 Te) was assessed and the zero bias dynamic resistance area product (R 0 A) was measured as >5 9 10 4 X cm 2 under stray illumination.
The design of present generation uncooled Hg1−xCdxTe infrared photon detectors relies on complex heterostructures with a basic unit cell of type ṉ+/π/p̱+. We present an analysis of double barrier ṉ+/π/p̱+ mid wave infrared (x=0.3) HgCdTe detector for near room temperature operation using numerical computations. The present work proposes an accurate and generalized methodology in terms of the device design, material properties, and operation temperature to study the effects of position dependence of carrier concentration, electrostatic potential, and generation-recombination (g-r) rates on detector performance. Position dependent profiles of electrostatic potential, carrier concentration, and g-r rates were simulated numerically. Performance of detector was studied as function of doping concentration of absorber and contact layers, width of both layers and minority carrier lifetime. Responsivity ∼0.38 A W−1, noise current ∼6×10−14 A/Hz1/2 and D∗ ∼3.1×1010cm Hz1/2 W−1 at 0.1 V reverse bias have been calculated using optimized values of doping concentration, absorber width and carrier lifetime. The suitability of the method has been illustrated by demonstrating the feasibility of achieving the optimum device performance by carefully selecting the device design and other parameters.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.